Wyniki wyszukiwania dla: REFORMER TUBES

• Evaluation of reformer tubes degradation after long term operation

  Publikacja

  • J. Łabanowski

  - Journal of Achievements in Materials and Manufacturing Engineering - Rok 2010

  Purpose of this paper is to show the effect of long-term service at elevated temperatures on microstructural changes of cast steel reformer tubes made of the alloy IN-519 (24%Cr, 24%Ni, Nb). The relationship between mechanical properties and microstructure degradation is discussed. Investigations were performed on five tubes taken from ammonia reformer furnace. Tubes worked at temperature of 880C and 3,2 MPa pressure. The operation...

  Pełny tekst do pobrania w portalu

• Assessment of structural changes in IN-519 cast steel reformer tubes.

  Publikacja

  • J. Łabanowski

  - Rok 2005

  Przedstawiono zmiany struktury rur katalitycznych ze staliwa austenitycznego IN-519 po długotrwałej eksploatacji w reformerze metanu.

• Assessment of reformer tubes degradation during longterm service at elevated temperatures

  Publikacja

  • J. Łabanowski

  - Rok 2005

• The Effect of Long Term Service at Elevated Temperatures on Microstructure Degradation of Austenitic Reformer Tubes

  Publikacja

  • J. Łabanowski
  • M. Jurkowski
  • M. Landowski

  - Advances in Materials Science - Rok 2018

  The paper analyses the relationship between an increase of the inner diameter of tubes made of Manaurite XM cast steel and transformations occurring in their microstructure due to long-lasting operation in methane reformer. Examinations included metallographic analysis with light microscope (LM), scanning electron microscope (SEM) and microanalysis of the chemical composition of precipitates (EDX). It was indicated that there is...

  Pełny tekst do pobrania w portalu

• Effect of long term service at elevated temperatures on mechanical properties of Manaurite XM reformer tubes

  Publikacja

  • J. Łabanowski
  • M. Jurkowski
  • M. Landowski

  - Advances in Materials Science - Rok 2016

  Microstructure transformations occur in the Manaurite XM cast steel tubes during long-term operation in the reformer furnace were revealed and described. The rela tionship between mechanical properties, an increase of internal diameter of the tube and microstructure degradation is discussed. Static tensile test was performed on two types of samples with different shapes. It has been shown differences in the results of tests...

  Pełny tekst do pobrania w portalu

• Performer

  Czasopisma

  ISSN: 2544-0896

• Fuels and Lubes International

  Czasopisma

  ISSN: 0117-9470

• Flow boiling of R22 and R134 a in enhanced tubes.

  Publikacja

  • J. Cieśliński
  • W. Targański

  - Rok 2003

  Przedstawiono wyniki badań wrzenia R22 oraz R134a w rurkach gładkich i o rozwiniętej powierzchni: mikrożebrowanej i śrubowo-formowanej. Podano opis stanowiska badawczego, procedury pomiarowej oraz metody obliczania średniego współczynnika przejmowania ciepła. Omówiono wyniki badań eksperymentalnych na tle danych cytowanych w literaturze, a także w porównaniu do wybranych korelacji.

• Sensitivity study of correlation for flow boiling in tubes.

  Publikacja

  • D. Mikielewicz
  • J. Białas

  - Rok 2005

  W referacie skupiono uwagę na szczegółowym zbadaniu wpływu wybranych typów modeli, opisujących współczynnik oporu przepływu oraz współczynnik przejmowania ciepła dla wrzenia w przepływie na korelację dla wrzenia w przepływie ( wyprowadzoną dla rur o konwencjonalnych wymiarach -półempiryczny model Mikielewicza ). Otrzymane wyniki porównano z danymi eksperymentalnymi.

• Single‐walled carbon nanotubes as nanotest tubes

  Publikacja

  • E. Borowiak‐Palen
  • E. Mijowska

  - physica status solidi (b) - Rok 2007

  Pełny tekst do pobrania w serwisie zewnętrznym