Selection of the lambda parameter for DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure
Dane BadawczeThis dataset contains results of selection of the lambda parameter for Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. Used lambdas: 5 x 10^(-3), 1 x 10^(-3), 5 x 10^(-4) and 1 x 10^(-4)....
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes at different oxygen partial pressures
Dane BadawczeIn this dataset are presented results of the polarization resistance of SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at 800 °C. The measurement temperature range was between 800 °C and 500 °C. Applied different oxygen partial pressure flow was: 1%, 20% and 100% pO2. Results converted to electrode surfaces area and dived by two electrodes. All...
-
Performance of Haemophilus influenzae impedimetric biosensors based on screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy studies of SPCE electrodes containing boron-doped diamond BDD foils and functionalized towards detection of Protein D and Haemophilus influenzae.
-
Distribution of Relaxation Times analysis results of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C) as a function of oxygen partial pressure at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode as a function of oxygen partial pressure at 800 °C. Electrode was sintered at 1000 °C and measured at different oxygen partial pressures (10% pO2, 1% pO2, 0.1% pO2).
-
Dual role of oxygen-related defects in the luminescence kinetics of AlNMn2+
Dane BadawczeThis dataset presents the impact of temperature and pressure on AlN:Mn2+ luminescence kinetics. Unusual behavior of Mn2+ optical properties during UV excitation is observed, where a strong afterglow luminescence of Mn2+ occurs even at low temperatures. When the temperature increases, the contribution of the afterglow luminescence is further enhanced,...
-
Nutrients, oxygen and suspended matter - Gdansk Deep (2001-2005)
Dane BadawczeThe results show short-term changes in the concentration of nutrients (nitrates, nitrites, ammonium ions, phosphates and total forms of nitrogen and phosphorus), dissolved oxygen and suspended particulate matter - SPM and its main components (organic carbon - POC, nitrogen - PON, phosphorus - TPP) in the water column of the Gdańsk Deep (Gdańsk Bay).
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 600 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 600 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results converted...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using three R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated three R-CPE elements from equivalent circuit,...
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using two R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated two R-CPE elements from equivalent circuit,...
-
Electrical conductivity of the Sr0.86Ti0.65Fe0.35O3-d pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense Sr0.86Ti0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method. Studies were performed at different oxygen partial pressures (20%, 1% and 0.1%) under humidified (~4 vol%) gas flow rate of 50 ml min -1.
-
Electrical conductivity of the (Ce0.80Gd0.20)O1.90 pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense (Ce0.80Gd0.20)O1.90 (CGO-20) pellet. DC electrical conductivity measurements of CGO-20 were performed by the Van der Pauw method between 900 °C and 450 °C with 50 °C step. Studies were performed at different oxygen partial pressures (100%, 20% and 1%) under humidified (~4...
-
Ni-based compounds in multiwalled graphitic shell for electrocatalytic oxygen evolution reactions
Dane BadawczeThis study investigates Ni-based compounds (Ni, NiO, Ni3C) coated with a graphitic shell as electrocatalysts for the oxygen evolution reaction (OER). Electron paramagnetic resonance (EPR) and X-ray diffraction (XRD) are employed to identify the presence and contribution of Nickel ions (Ni0, Ni2+, Ni3+) and determine the phase composition. Electrochemical...
-
SEM images of cross sections of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains cross sectional images of the porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes symmetric cells samples interface. Here are presented images of electrodes sintered at 950 °C, 1000 °C and 1050 °C. Images were obtained using a FEI Quanta FEG 250 Scanning Electron Microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum...
-
Topography studies of screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains topography examination of SPCE containing boron-doped diamond BDD foils done with scanning electron microscope. Different points mark different electrode spots: A) working electrode, B) reference electrode, C) counter electrode, D) pads.
-
Scanning electron microscopy (SEM) images of the boron-dopied diamond surfaces
Dane BadawczeThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of diamond electrodes on silicon substrates. The diamond surface is characterized by ultra-crystalline diamonds obtained by CVD synthesis.
-
Oxygen partial pressure and temperature dependence of Gerischer element of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of Gericher element at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C)and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent circuit...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of series resistance (R) at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Series resistance (at 800 °C - 500 °C) of the Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C, 1000 °C and 1050 °C. The measurement temperature range was between 800 °C and 500 °C in stationary air. Results converted to electrode surfaces area.
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element series resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Electrochemical studies for screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains electrochemical examination of SPCE paste and SPCE containing boron-doped diamond BDD foils. The studies include kinetics analyses with cyclic voltammetry and electrochemical impedance spectroscopy with different redox probes: hexacyanoferrate(III) and Hexaammineruthenium(III) and potentiostatic open circuit potential at different...
-
Chemical and structural studies of screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains chemical analyses and structural studies by XPS and Raman spectroscopy, carried out for SPCE containing boron-doped diamond BDD foils done with scanning electron microscope. Different points for XPS analysis mark different electrode spots: A) working electrode, B) reference electrode, C) counter electrode, D) pads.
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Dane BadawczeThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...
-
Area specific resistance (at 800 °C - 500 °C) of the Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C, 1000 °C and 1050 °C. The measurement temperature range was between 800 °C and 500 °C in stationary air. Results converted to electrode surfaces...
-
Oxygen partial pressure and temperature dependence of low frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of low frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of middle frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of low frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of low frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of middle frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Influence of sintering temperature of porous SrTi0.30Fe0.70O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Influence of sintering temperature of porous SrTi0.50Fe0.50O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...