Effect of nitrogen doping on TiOxNy thin film formation at reactive high-power pulsed magnetron sputtering
Abstrakt
The paper is focused on a study of formation of TiOxNy thin films prepared by pulsed magnetron sputtering of metallic Ti target. Oxygen and nitrogen were delivered into the discharge in the form of reactive gases O2 and N2. The films were deposited by high-power impulse magnetron sputtering working with discharge repetition frequency f = 250 Hz at low (p = 0.75 Pa) and high (p = 10 Pa) pressure. The substrates were on floating potential and thermally stabilized at room temperature during the deposition process. Post-deposition thermal annealing was not employed. The chemical composition from x-ray photoelectron spectroscopy diagnostic reveals formation of TiOxNy structure at low flow rate of oxygen in the discharge gas mixture. This result is confirmed by XRD investigation of N element's incorporation into the Ti-O lattice. Decrease in band-gap to values Eg ~ 1.6 eV in TiOxNy thin film is attributed to formed Ti-N bonds. The discharge properties were investigated by time-resolved optical emission spectroscopy. Time evolution of particular spectral lines (Ar+, Ti+, Ti) is presented together with peak discharge current.
Autorzy (7)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF PHYSICS D-APPLIED PHYSICS
nr 43,
strony 5203 - 5210,
ISSN: 0022-3727 - Język:
- angielski
- Rok wydania:
- 2010
- Opis bibliograficzny:
- Stranak V., Quaas M., Bogdanowicz R., Hartmut S., Hubicka Z., Tichy M., Hippler R.: Effect of nitrogen doping on TiOxNy thin film formation at reactive high-power pulsed magnetron sputtering// JOURNAL OF PHYSICS D-APPLIED PHYSICS. -Vol. 43, nr. Iss. 28 (2010), s.5203-5210
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 129 razy
Publikacje, które mogą cię zainteresować
Influence of reactive oxygen species during deposition of iron oxide films by high power impulse magnetron sputtering.
- V. Stranak,
- Z. Hubicka,
- M. Cada
- + 4 autorów
Physical properties of homogeneous TiO2 films prepared by high power impulse magnetron sputtering as a function of crystallographic phase and nanostructure
- V. STRAňáK,
- M. Čada,
- M. Quaas
- + 7 autorów
Properties of Barium Cerate-Zirconate Thin Films
- P. Winiarz,
- M. S. Covarrubias Campos,
- M. Sriubas
- + 6 autorów
Mobility measurements in oxide semiconductors
- E. Prociów,
- M. S. Łapiński,
- J. Domaradzki
- + 3 autorów