The 430L stainless steel powder with a mean particle size of 95 μm was studied to determine its high-temperature oxidation properties. Continuous thermogravimetric measurements were carried out for 100 h in air at temperatures in the range of 600–850 °C. Even though a considerable amount of Cr (up to ˜5 wt.% Cr) inside the grains was depleted – especially inside small grains – no breakaway oxidation was observed. This indicates that both the remaining Cr and the formed chromia scale remained protective with regard to the metallic core until the Cr concentration reached very low levels.
Citations
-
1 8
CrossRef
-
0
Web of Science
-
2 0
Scopus
Authors (6)
-
Tomasz Brylewski
- Akademia Górniczo-Hutnicza w Krakowie Wydział Inżynierii Materiałowej i Ceramiki
-
K. H. Andersen
- Technical University of Denmark .
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuł w czasopiśmie wyróżnionym w JCR
- Published in:
-
CORROSION SCIENCE
no. 149,
pages 100 - 107,
ISSN: 0010-938X - Language:
- English
- Publication year:
- 2019
- Bibliographic description:
- Karczewski J., Brylewski T., Miruszewski T., Andersen K., Jasiński P., Molin S.: High-temperature kinetics study of 430L steel powder oxidized in air at 600–850 °C// CORROSION SCIENCE. -Vol. 149, (2019), s.100-107
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.corsci.2019.01.005
- Verified by:
- Gdańsk University of Technology
seen 166 times