High-temperature kinetics study of 430L steel powder oxidized in air at 600–850 °C

Abstrakt

The 430L stainless steel powder with a mean particle size of 95 μm was studied to determine its high-temperature oxidation properties. Continuous thermogravimetric measurements were carried out for 100 h in air at temperatures in the range of 600–850 °C. Even though a considerable amount of Cr (up to ˜5 wt.% Cr) inside the grains was depleted – especially inside small grains – no breakaway oxidation was observed. This indicates that both the remaining Cr and the formed chromia scale remained protective with regard to the metallic core until the Cr concentration reached very low levels.

Cytowania

  • 1 6

    CrossRef

  • 0

    Web of Science

  • 1 7

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
CORROSION SCIENCE nr 149, strony 100 - 107,
ISSN: 0010-938X
Język:
angielski
Rok wydania:
2019
Opis bibliograficzny:
Karczewski J., Brylewski T., Miruszewski T., Andersen K., Jasiński P., Molin S.: High-temperature kinetics study of 430L steel powder oxidized in air at 600–850 °C// CORROSION SCIENCE. -Vol. 149, (2019), s.100-107
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.corsci.2019.01.005
Weryfikacja:
Politechnika Gdańska

wyświetlono 113 razy

Publikacje, które mogą cię zainteresować

Meta Tagi