Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 300 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 150 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 100 mm stroke subjected only to a mass load of 750 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 300 mm stroke subjected only to a mass load of 1040 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 100 mm stroke subjected only to a mass load of 1530 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 150 mm stroke subjected only to a mass load of 1640 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 1100 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Wind speed, wind direction and solar radiation datasets; wind and solar energy resources analysis
Open Research DataDataset contain the results of wind speed, wind direction and solar radiation for wind and solar energy resources analysis performed in years 2008 and 2009. Application for efficiency and profitability of solar and wind power plants anaylsis and for energy generation forecasting algorithms design and anaysis. Datasets used in doctoral dissertations,...
-
Simulation of perovskite-based CuI/CH3NH3PbI3/TiO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/TiO2 model structure (Model 1) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/SnO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/SnO2 model structure (Model 2) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/ZnO solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/ZnO model structure (Model 3) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Instantaneous power signal measurements for bearing diagnostics
Open Research DataBearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous current and voltage power supplied to the engines. Bearing damage causes the appearance of deformations, which are in the form of additional harmonic components...
-
Analysis of the instantaneous power signal for bearing diagnostics -bearing damaged
Open Research DataThe attached dataset contains the measurement results of the instantaneous values of current and voltage, recorded during the diagnostics of a damaged bearing. Bearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous...
-
Analysis of the instantaneous power signal for bearing diagnostics - bearing undamaged
Open Research DataThe attached dataset contains the measurement results of the instantaneous values of current and voltage, recorded during the diagnostics of an undamaged bearing. Bearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous...
-
The structure of revenues of non-public universities in 2010 from didactic activity by sources of financing (in%)
Open Research DataIncome from teaching activities of non-public universities accounted for almost 1/5 of income from teaching activities of all types of universities. Non-public universities generated the highest revenues from fees for teaching classes, which accounted for over half of the revenues from this title in relation to all universities.The average cost of education...
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 4-8h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 4-8h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #24 - #25.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #24 (upper, rotating), #25 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #30 - #31.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #30 (upper, rotating), #31 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #20 - #21.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #20 (upper, rotating), #21 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #22 - #23.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #22 (upper, rotating), #23 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #26 - #27.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #26 (upper, rotating), #27 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h. High frequency burst recording.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. High frequency burst recording.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21,...