Complex modulus of Cement Bitumen Treated Material Mixture (28 days of curing at 20C)
Open Research DataDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with 3 combinations of binding agents: 2% cement, 6% emulsion (C2E6), 6% cement, 6% emulsion (C6E6), 6% cement, 2% emulsion (C6E2). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains...
-
Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
Open Research DataFatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
-
Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (Direct tension, over 28 days of curing at 20C)
Open Research DataFatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (Direct tension, over 28 days of curing at 20C)
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 laboratory mixed/laboratory compacted (7-365 days of curing at 20C)
Open Research DataDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in laboratory conditions on the basis of materials obtained from...
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 field mixed/laboratory compacted (7-365 days of curing at 20C)
Open Research DataDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in the field conditions and later compacted in laboratory. Mixture...
-
Deformation Sweep Test of Cement Bitumen Treated Material Mixture C3E5.5 (field obtained material; over 28 days of curing at 20C)
Open Research DataDataset presents data of results of deformation sweep test determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100...
-
Deformation Sweep Test of Cement Bitumen Treated Material Mixture C3E5.5 (field cores; field curing)
Open Research DataDataset presents data of results of deformation sweep test determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100...
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 cores obtained from the field section (28-365 days of curing at the field and later in laboratory at 20C)
Open Research DataDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Specimen were obtained from the field at 28, 180, 270 and 365 days after compaction....
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
Open Research DataDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100 mm, h=130 mm. Specimen...
-
Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C, field cores)
Open Research DataDataset presents data of fatigue life determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100 mm, h=48,4 - 70,9 mm.
-
Deflection measurement of field section with pavement with base course made of Cement Bitumen Treated Material Mixture C3E4 (28, 180, 270, 365 days after compaction)
Open Research DataDataset presents data of deflections determined for pavement with base course made of cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in stationary plant and compacted...
-
Effect of particle size of aluminosilicate microspheres on the change of hydration heat of cement mortars and selected physical, chemical, and mechanical properties.
Open Research DataThis subject of the work is the study of selected properties of cement mortars containing two fractions of aluminosilicate microspheres with grain size in the range of 125 to 250 μm and from 250 to 500 μm. Mortar mixtures with ordinary Portland cement (OPC 42.5R) and three substitution rates of cement by microspheres, 1.5%, 3.5%, and 5.0%, were investigated....
-
Acoustic emission signals in concrete beams under 3-point bending (polyolefin and steel fibre concrete)
Open Research DataThe DataSet contains the results of the mechanical behaviour of concrete beams with dimensions 40 x 40 x 160 cm3 under the 3-point bending. All specimens were manufactured based on the same concrete mixture composed of cement CEM I 42.5R (380 kg/m3), water (165 kg/m3), aggregate 0/2 mm (648 kg/m3), aggregate 2/8 mm (426 kg/m3), aggregate 8/16 mm (754...
-
Measurements of the heat of hydration released by concrete specimens cured under adiabatic conditions
Open Research DataThe DataSet contains measurements of heat of hydartion of concrete cubes (150 x 150 x 150 mm) cured under adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...
-
Concrete temperature measurements of cubic specimens cured under isothermal and semi-adiabatic conditions
Open Research DataThe DataSet contains temperature measurements of concrete cubes (150 x 150 x 150 mm) cured under isothermal and semi-adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...