Search results for: lubrication

• CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN  over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...

• TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  3 min. The test...

• TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  20 min. The test...

• SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  3 min. The test...

• TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  90 min. The test...

• TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC  over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  3 min. The...

• CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  6 min. The test...

• SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. distilled water lubrication

  Wear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC  over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration  3 min. The test...

• DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  Wear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....

• DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  Wear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....

• TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....

• SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...

• CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN  over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....

• TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....

• TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...

• SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...

• TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....

• CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21

  Open Research Data

  open access

  • A. Neyman
  • J. Łubiński
  • A. Olszewski
  • K. Druet

  - series: Wear of ultra thin PVD ceramic coatings on stainless steel in ring-on-ring sliding w. saline solution (0.9%) lubrication

  Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN  over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...

• Grease effect on fretting wear of mild steel

  Publication

  • A. Neyman
  • J. Sikora

  - INDUSTRIAL LUBRICATION AND TRIBOLOGY - Year 2008

  Na stanowisku laboratoryjnym przeprowadzono badania zużycia frettingowego miękkiej stali smarowanej mineralnymi i syntetycznymi smarami zawierającymi także różne dodatki: grafit dwusiarczek molibdenu ZDDP i ditiocarbamat molibdenu, w różnych stężeniach.Badania wykazały istotny wpływ konsystencji smaru i jego właściwości smarnych na zużycie frettingowe miękkiej stali oraz zróżnicowany wpływ testowanych dodatków. Obecność smaru...

• The problems of resistance to scuffing of heavily loaded lubricated friction joints with WC/C-coated parts

  Publication

  • R. Michalczewski
  • W. Piekoszewski
  • W. Tuszynski
  • M. Szczerek

  - INDUSTRIAL LUBRICATION AND TRIBOLOGY - Year 2014

  Full text to download in external service

• Centrifugal magnetic fluid seals

  Publication

  • L. Matuszewski
  • N. Canter

  - TRIBOLOGY & LUBRICATION TECHNOLOGY - Year 2018

  Seals perform an important and at times overlooked function in a lubricant system. They prevent or minimize the movement of the lubricant between two surfaces and also minimize the level of contamination in the system. Seals are divided into static and dynamic types. Static seals operate in systems where the mating surfaces do not move relative to each other. In contrast, dynamic seals operate under conditions where the mating surfaces...

  Full text available to download

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #24 - #25.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #24 (upper, rotating), #25 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #30 - #31.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #30 (upper, rotating), #31 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #20 - #21.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #20 (upper, rotating), #21 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #22 - #23.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #22 (upper, rotating), #23 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #26 - #27.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - series: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #26 (upper, rotating), #27 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Optical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...

• Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Optical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...

• Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Optical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...

• Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04

  Open Research Data

  open access

  • J. Łubiński
  • K. Druet

  - series: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Optical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...

• Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 4-8h.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - series: Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication.

  Wear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 4-8h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21,  #22-#23,  #24-#25,  #26-#27,...

• Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - series: Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication.

  Wear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21,  #22-#23,  #24-#25,  #26-#27,...

• Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h. High frequency burst recording.

  Open Research Data

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - series: Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication.

  Wear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. High frequency burst recording.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21,...

• Wojciech Litwin dr hab. inż.

  People

  Zakład Wyposażenia Okrętu, Faculty of Mechanical Engineering and Ship Technology, Institute of Ocean Engineering and Ship Technology

  1992÷1996 - study on Mechanical Department at Gdansk University of Technology1996 – employed in the Faculty of Ocean Engineering and Ship Technology at the Gdansk University of Technology2004 – PhD2014 – habilitation2016 - vice dean for science at Faculty of Ocean Engineering2020 - dean of the Faculty of Ocean Engineering2021 - head of Institute of Naval Architecture He participated in a number of designing and research programs...

• Application of the Optimization Methods to the Search of Marine Propulsion Shafting Global Equilibrium in Running Condition

  Publication

  • A. Ursolov
  • Y. Batrak
  • W. Tarełko

  - Polish Maritime Research - Year 2019

  Full film hydrodynamic lubrication of marine propulsion shafting journal bearings in running condition is discussed. Considerable computational difficulties in non-linear determining the quasi-static equilibrium of the shafting are highlighted. The approach using two optimization methods (the particle swarm method and the interior point method) in combination with the specially developed relaxation technique is proposed to overcome...

  Full text available to download

• Anomalous Behavior of Hyaluronan Crosslinking Due to the Presence of Excess Phospholipids in the Articular Cartilage System of Osteoarthritis

  Publication

  • P. Bełdowski
  • P. Weber
  • T. Andrysiak
  • W. Auge
  • D. Ledziński
  • T. DeLeon
  • A. Gadomski

  - INTERNATIONAL JOURNAL OF MOLECULAR SCIENCES - Year 2017

  Lubrication of articular cartilage is a complex multiscale phenomenon in synovial joint organ systems. In these systems, synovial fluid properties result from synergistic interactions between a variety of molecular constituent. Two molecular classes in particular are of importance in understanding lubrication mechanisms: hyaluronic acid and phospholipids. The purpose of this study is to evaluate interactions between hyaluronic acid...

  Full text available to download

• Tribological test for evaluation of CF30 Black PEEK

  Open Research Data

  open access

  • T. Żochowski

  Sample numner BL03 and BL04 made of PEEK CF30 (black color) tribologicaly tested with sliding speed up to 1,8 m/s and up to 14 MPa of nominal load under water lubrication.

• Investigating lubricants behaviour in microgravity for vibration damping purposes

  Publication

  • S. R. Krawczuk
  • A. Dąbrowski

  - Year 2021

  Vibration is one of the harshest environments an object is exposed to during and after launch into space on a launch vehicle. Such vibrations should be damped to avoid destruction of the spacecraft or its elements. Currently, active and material damping is used. A possibility of using lubrication as the damping factor is suggested by some research. MoS2 is a typical solid lubricant used in space applications. Its properties vary...

  Full text available to download

• RESEARCH ON HYDRODYNAMIC PEEK JOURNAL BEARINGS LUBRICATED WITH WATER AND OIL

  Publication

  • T. Żochowski
  • A. Olszewski
  • M. Wasilczuk

  - TRIBOLOGIA - Year 2023

  The main purpose of the research was to determine the possibilities and experimentally test the benefits of replacing conventional oil lubrication with ecological water lubrication. Tests were carried out on a test rig for hydrodynamic radial bearings under conditions representative of the expected applications for the bearing in water turbines. Bearings made from the polymer material PEEK (polyether ether ketone) were tested under static...

  Full text available to download

• Combined thrust radial bearing of a submarine main shaft – Design and analysis of failure

  Publication

  • M. Wasilczuk
  • F. Wasilczuk

  - ENGINEERING FAILURE ANALYSIS - Year 2020

  This paper presents an analysis of the combined thrust radial bearing of a submarine propulsion shaft. The lubrication system of the bearing is based on a fixed ring. The efficiency of the lubrication system depends on the shaft speed and temperature, which affects oil viscosity. In turn, the thrust bearing load also depends on the rotational speed of the shaft, because as the speed increases, the drag of the ship increases simultaneously,...

  Full text available to download