Rok 2018
-
Oxidation and hydrogen behavior in Zr-2Mn alloy
PublikacjaThe purpose of the present research was to determine the oxidation and hydrogenation behavior in the new Zr-2Mn alloy. The oxidation of alloy was performed at temperatures between 350°C and 900°C for 30 minutes. The hydrogen charging was made for 72 h at a current density 80 mA/cm2. The charged samples were heat treated at 400°C for 4 h to obtain a uniform hydrogen profile content across the sample. The oxidation resulted in an...
Rok 2017
-
3D Printing of Metallic Implants
PublikacjaThe fabrication of various elements, solid and open porous structures of stainless steel and Ti alloy is described. The process was started with the design of 3D models in CAD/CAM system. The 3D models were transformed into *.stl files and then the manufacturing process of the real structures by means of the selective laser melting with the SLM Realizer 100 3D printer was made. The paper shows the porous specimens made for possible...
-
Deposition of phosphate coatings on titanium within scaffold structure
PublikacjaPurpose: Existing knowledge about the appearance, thickness, and chemical composition of phosphate coatings on titanium inside porous structures is insufficient. Such knowledge is important for the design and fabrication of porous implants. Methods: Metallic scaffolds were fabricated by selective laser melting of 316L stainless steel powder. Phosphate coatings were deposited on Ti sensors placed either outside the scaffolds or...
-
Electrophoretic deposition (EPD) of nanohydroxyapatite - nanosilver coatings on Ti13Zr13Nb alloy
PublikacjaTitanium and its alloys are the biomaterials most frequently used in medical engineering, especially as parts of orthopedic and dental implants. The surfaces of titanium and its alloys are usually modified to improve their biocompatibility and bioactivity, for example, in connection with the deposition of hydroxyapatite coatings. The objective of the present research was to elaborate the technology of electrophoretic deposition...
-
Hydrogen degradation of pre-oxidized zirconium alloys
PublikacjaThe presence of the oxide layers on Zr alloys may retard or enhance the hydrogen entry and material degradation, depending on the layer features. This research has been aimed to determine the effects of pre-oxidation of the Zircaloy-2 alloy at a different temperature on hydrogen degradation. The specimens were oxidised in laboratory air at 350°C, 700°C, and 900°C. After, some samples were tensed at 10-5 strain rate and simultaneously...
-
Properties of Composite Oxide Layers on The Ti13Nb13Zr Alloy
PublikacjaThe development of composite oxide layers on the Ti13Nb13Zr alloy, their structure and properties have been demonstrated. Two subsequent methods were applied to prepare the composite layers. During the first stage gas oxidation produced a solid oxide layer, and subsequently oxide nanotubes were produced by using an electrochemical method. Scanning electron microscopy (SEM), chemical analysis, energy dispersive X-ray spectroscopy...
-
Prosthetic Elements Made of the Ti-13Zr-13Nb Alloy by Selective Laser Melting
PublikacjaThe fabrication of the prosthetic foundations and bridges from the Ti-13Zr-13Nb alloy is described. The process was started from CAD/CAM design of 3D models of the foundations based on scanning of patient`s mouth. Next, 3D models were transformed into *.stl files for the manufacturing stage and then the manufacturing process by means of the selective laser melting with the SLM Realizer 100 equipment was made. The intrinsic structure...
-
Selective Laser Melting of Ti Alloy for Manufacturing The Prosthetic Elements
PublikacjaThe selective laser melting (SLM) is the additive manufacturing method of custom-designed parts. The used materials and the applications are various, including medicine. The titanium and its alloys are materials for which the dimensional quality, surface smoothness and no or extremely low porosity are difficult to reach. In this paper, the successful attempt to obtain by SLM the individually designed prosthetic bridges is described....
-
THE USE OF THE Ti-13Zr-13Nb ALLOY POWDER FOR MANUFACTURING OF PROSTHETIC PARTS BY SELECTIVE LASER MELTING
PublikacjaThe 3D printing is a manufacturing technique belonging to the additive methods able to prepare the designed parts for various purposes. The present reasearch was aimed to fabricate the prosthetic foundations and bridges made of the new Ti-13Zr-13Nb alloy by the selective laser melting (SLM) of a metal powder. The scanning electron examinations and micro scanning tomography were used to investigate the surface quality and intrinsic...
Rok 2016
-
EFFECT OF SURFACE STATE AND STRESS ON AN OXIDATION OF THE ZIRCALOY-2 ALLOY
PublikacjaZr alloys are widely used as materials for nuclear fuel pellets in the nuclear industry. In the case of the LOCA or RIA happen, a temperature may locally reach high values. Even if the high temperature maintains shortly, the zirconium oxides may become permeable, absorb hydrogen appearing in cooling water from decomposition reaction and crack because of formation and brittle failure of hydrides. Such model cannot so far take into...
-
Electrochemically assisted deposition of hydroxyapatite on Ti6Al4V substrates covered by CVD diamond films — Coating characterization and first cell biological results
PublikacjaAlthough titaniumand its alloys are widely used as implant material for orthopedic and dental applications they show only limited corrosion stability and osseointegration in different cases. The aim of the presented research was to develop and characterize a novel surface modification system from a thin diamond base layer and a hydroxyapatite (HAp) top coating deposited on the alloy Ti6Al4V widely used for implants in contact with bone....
Rok 2015
-
Influence of Staphylloccoccus bacteria adhesion on the degradation of the Ti6Al4V alloy
PublikacjaThe paper deals with bacteria adhesion and the degradation of the Ti6Al4V alloy
-
The bahaviour of selected silver coated body implants in presence of various bacteria
PublikacjaThe article deals with implants covered with silver nanoparticles and its influence on bacteria adhesion.
-
THE POSSIBILITY OF USE OF LASER-MODIFIED Ti6Al4V ALLOY IN FRICTION PAIRS IN ENDOPROSTHESES
PublikacjaThe purpose of this paper is to show results of laser treatment at cryogenic conditions of the Ti6Al4V alloy used for orthopedic applications. That modification process ought to bring beneficial changes of microstructure and residual stresses in the surface layer. The paper presents the abrasive wear of the base and laser remelted material in association with ceramics Al2O3. Despite the surface cracking after laser treatment the...
-
Wpływ modyfikacji laserowej stopu Ti13Nb13Zr na mikrostrukturę powłok hydroksyapatytowych
PublikacjaDotychczasowe badania powierzchni wszczepów tytanowych dla chirurgii kostnej wykazały, że osteointegracja na powierzchniach rozwiniętych jest znacznie szybsza niż na powierzchniach gładkich, co za tym idzie chropowatość powierzchni implantu ma bardzo duży wpływ na adhezję składników środowiska biologicznego. W artykule przedstawiono wstępne wyniki badań dotyczące wpływu chropowatości powierzchni stopu Ti13Nb13Zr o bardzo małym...
Rok 2014
-
Environmental degradation of Ti alloys in artificial saliva and a role of fluorides
PublikacjaThe titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization...
-
Evaluation of Wear Resistance of Ti alloys used for elements friction of knee endoprosthesis
PublikacjaThe paper presents research results of resistance to abrasive wear of titanium alloys: Ti6Al4V (commonly used) and Til3Nb13Zr (alloy of new generation) in association with polyethylene (UHMW-PE) predisposed for elements on pair of the knee endoprosthesis. The results were analysed from the point of possibility of an use of new generation titanium alloys as components of such implants. The tests of resistance to abrasive wear of...
-
Morphology and properties of nanotubular oxide layer on the Ti13Zr13Nb alloy
PublikacjaThe Ti13Zr13Nb alloy in solid and porous form was oxidised. The constant voltage 20 V, oxidation time 0.5 and 1 h, and 1 M H3PO4 (orthophosphoric acid) with addition of HF (hydrofluoric acid) as a test solution were applied. SEM (Scanning Electron Microscope) examinations of surface, EDS (Energy Dispersive X-ray Spectroscopy) chemical analysis, nanohardness and nano-scratch tests, and corrosion potentiokinetic tests at various...
-
Nanotubular oxide layers and hydroxyapatite coatings on ‘Ti–13Zr–13Nb’ alloy
PublikacjaThe presented research was aimed to determine the mechanical properties of the nanotubular oxide layer covered with hydroxyapatite coating. The Ti–13Zr–13Nb alloy was oxidised in 1M phosphoric acid with an addition of 0?5% HF for HF solution at 20 V voltage. The electrochemically assisted deposition of hydroxyapatite was performed at cyclic polarisation in NH4H2PO4 and CaCl2 solution at 80uC. The mechanical properties were determined...
Rok 2013
-
CDIO IN GDANSK: PEOPLE-ORIENTED STRATEGY
PublikacjaThe CDIO system implementation in Poland meets problems and Gdansk University of Technology (GUT) is still a single higher education institution in Poland accepted as the member of CDIO Initiative. The paper detects and characterizes the existing problems to be solved. In particular, the different groups of people are considered as supporters or fighters against CDIO idea, their attitudes being considered and applied strategy demonstrated. The...
-
Effects of the preheating laser treatment on microstructure and corrosion resistance of Ti6Al4V bioalloy
PublikacjaThe laser remelting of the Ti6Al4V alloy was made on specimens pre-heated at elevated temperatures. The laser treatment effected in change of microstructures of surface layers and an appearance of blisters and numerous cracks. The corrosion tests demonstrated the decrease in corrosion resistance for each preheating temperature. The observed effects were attributed to negative influence of excessive compressive stresses with no...
-
Elctrochemical oxidation and corrosion resistance of the Ti13Nb13Zr alloy
PublikacjaThis paper presents the results of oxidation and corrosion tests carried out on titanium alloy Ti13Nb13Zr. The oxide film was prepared by electrochemical environment 2M H3PO4 for 30 min and 1 h, at a constant voltage 40V. The tests of corrosion resistance were performed by potentiostatic method in Ringer's solution at different pH values: 7, 5 and 3. The change in an appearance of surface and the increase in corrosion resistance...
-
Ocena odporności na zużycie ścierne stopów Ti na elementy pary trącej endoprotez stawu kolanowego
PublikacjaNajczęściej stosowanym biomateriałem tytanowym na elementy endoprotez stawu kolanowego jest stop Ti6Al4V. Z uwagi na zawartość wanadu, zaliczanego do pierwiastków o dużej toksyczności podejmowane są działania w kierunku zastąpienia wskazanego stopu - stopami bezwanadowymi. Jednym z najbardziej obiecujących jest stop Ti13Nb13Zr zawierający w swoim składzie jedynie pierwiastki witalne, niewywołujące stanów zapalnych i odczynów...
Rok 2012
-
Bioactive core material for porous load-bearing implants
PublikacjaSo far state of knowledge on biodegradable materials is reviewed. Among a variety of investigated materials, those composed of polymers and ceramics may be considered as only candidates for a core material in porous titanium alloy. The collagen and chitosan among natural polymers, polyhydroxy acids among synthetic polymers, and hydroxyapatite and tricalcium phosphate among ceramics are proposed for further research. Three essential...
-
Effects of Laser Remelting at Cryogenic Conditions on Microstructure and Wear Resistance of the Ti6Al4V Alloy Applied in Medicine
PublikacjaThe titanium and its alloys can be subjected to surface treatment, including laser treatment. In this work a new laser treatment at cryogenic conditions of Ti6Al4V alloy has been described. The work has been aimed at establishing whether such surface treatment could be suitable for implants working under wear in biological corrosive environment. The remelting has been made with the use of CO2 continuous work laser at laser power...
-
Environmental Degradation of Engineering Materials & Materials Engineering and Technologies
Publikacja -
Environmental degradation of titanium alloy in artificial saliva
PublikacjaThe titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization...
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Formation of Porous Structure of the Metallic Materials Used on Bone Implants
PublikacjaResearch on improvement of structure and fabrication methods of the bone implants are carried out for many years. Research are aimed to shape the structures, that will have a Young's modulus value similar to the value of the human bones Young's modulus. Depending on theporosity, Young's moduli can even be tailored to match the modulus of bone closer than solid metals can, thus reducing the problems associated with stress shielding...
-
Materials Design for the Titanium Scaffold Based Implant
PublikacjaThe main objective of here presented research is a design the scaffold/porous titanium(Ti) alloy based composite material demonstrating better biocompatibility, longer lifetime andbioactivity behaviour for load-bearing implants. The development of such material is proposed bymaking a number of consecutive tasks. Modelling the mechanical, biomechanical and biologicalbehavior of porous titanium structure and an elaboration of results...
-
Materials Design for the Titanium Scaffold Based Implant
PublikacjaThe main objective of here presented research is a design the scaffold/porous titanium(Ti) alloy based composite material demonstrating better biocompatibility, longer lifetime andbioactivity behaviour for load-bearing implants. The development of such material is proposed bymaking a number of consecutive tasks. Modelling the mechanical, biomechanical and biologicalbehavior of porous titanium structure and an elaboration of results...
-
Surface treatment of porous Ti13Nb13Zr alloy for biomedical applications
PublikacjaPrzeprowadzono badania materiału porowatego, przeznaczonego na implanty ortopedyczne, wytworzonego metodą metalurgii proszków ze stopu Ti13Nb13Zr. Proszki z badanego stopu uzyskano metodą rozpylania plazmowego. Otrzymano próbki o otwartej porowatej strukturze, stopniu porowatości do 68% i średniej wielkości porów w przedziale 30-150 mikrometrów. Obróbka próbek porowatych - utlenianie termiczne, chemiczne i/lub elektrochemiczne...
Rok 2011
-
Hydrogen-enhanced degradation and oxide effects in zirconium alloys for nuclear applications
PublikacjaThe zirconium alloys used in nuclear industry include mainly ZreSn and ZreNb alloys ofdifferent chemical composition, microstructure and susceptibility to both hydrogendegradation and oxidation. The hypothetic nuclear accidents can create a real danger tothe Zr alloys and stability of parts made of these alloys, and especially such as loss ofcoolant accident (LOCA) and reactivity initiated accidents (RIA). The hydrogen degradationcan...
-
Nanotechnologie i nanomedycyna
PublikacjaZastosowanie nanotechnologii w wytwarzaniu implantów, diagnozowaniu chorób oraz ich leczeniu.
-
Nanotechnologies in Development of Structural Materials and Biomaterials
PublikacjaThe nanometric materials and technologies resulted in nanostructures are reviewed. The examples of nanomaterials are shown. The typical nanotechnologies, including plastic deformation, mechanical attrition, controlled detonation, hot plasma jet synthesis, laser vaporisation, CVD and PVD, mechanical milling, annealing, ultrasonic irradiation, nanolithography, electrocrystallisation, electrospinning, sol-gel method, cryogenic laser-enhanced...
-
Porous biomaterial for orthopaedic implants based on titanium alloy
PublikacjaTytan i jego stopy są szeroko stosowane jako biomateriały dla zastosowań ortopedycznych. Badania związane z ich najlepszą odpornością na korozję i ścieranie, biozgodnością i bioaktywnością są stale prowadzone. Obecne badania koncentrują się również na projektowaniu i produkcji materiałów porowatych w oparciu o stopy np. Ti-13Nb-13Zr, które mogą być stosowane do wytwarzania implantów. Jedną z najbardziej efektywnych metod wytwarzania...
-
Preparation of nano-tubular oxide layers on titanium alloy Ti13Nb13Zr
PublikacjaThe article presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr preformed at different conditions. The oxide layers have been formed using electrochemical method in 2M H3PO4 + 0,3% HF solution for 30 min. and 1h at 20V constant voltage. The corrosion tests heve been made with poteniodynamic method in Ringer's solution at pH ranged 3 and 7. It has been shown that the nano-oxide films, which...
Rok 2010
-
Biocompatibility and bioactivity of bearing loaded metallic implants
PublikacjaPresentation of developed titanium alloy base composite materials possessing better biocompatibility, longer lifetime and bioactivity behavior for bearing loaded implants, e.g. hip joint and knee joint endoproshtesis.
-
Biocompatibility and bioactivity of load-bearing metallic implants
PublikacjaThe main objective of here presented research is to develop the titanium (Ti) alloy base composite materials possessing better biocompatibility, longer lifetime and bioactivity behaviour for load-bearing implants, e.g. hip joint and knee joint endoprosthesis. The development of such materials is performed through: modeling the material behaviour in biological environment in long time and developing of new procedures for such evaluation;...
-
Biocompatibility and Bioactivity of Load-Bearing Metallic Implants
PublikacjaThe main objective of here presented research is to develop the titanium (Ti) alloy base composite materials possessing better biocompatibility, longer lifetime and bioactivity behaviour for load-bearing implants, e.g. hip joint and knee joint endoprosthesis. The development of such materials is performed through: modeling the material behaviour in biological environment in long time and developing of new procedures for such evaluation;...
-
Degradation of metallic implants
PublikacjaPresence of metallic implants made of stainless steels, Co and Ti alloys is sometimes followed by some undesired allergic reactions and inflammatory processes and consequently the necessity of reimplantation.
-
Influence of laser melting on surface layer properties of titanium alloy Ti6Al4V
PublikacjaIn time of rapid technology and medicine progress, implants are becoming more widely used in the human body, ranging from dental implants, stabilizing plates, screws, orthopaedic prostheses. For example, there are many types of hip prostheses used for hip replacement as well as various types of materials used for these orthopaedic prostheses. Properties of titanium alloys used in hip prostheses combined with good strength properties,...
-
Nowe metody badań korozji i pękania wodorowego materiałów eksploatowanych w umiarkowanych warunkach
PublikacjaPrzedstawiono założenia testu niskocyklowego zmęczenia nawodorowanego materiału oraz oceny odporności korozyjnej biomateriału bazującej na oznaczaniu ilości metalu w roztworze.
-
Properties of surface layers of titanium alloy Ti6Al4V after laser melting processes
PublikacjaThe article presents the investigation results of titanium alloy Ti6Al4V surface layer after laser melting process. The process of laser melting was performed using Nd-YAG laser. The evaluation of structure of the alloy as well as hardness and chemical composition was performed. It was shown that laser melting changes the structure and properties of titanium alloy Ti6Al4V and process parameters as scanning speed affects the thickness...
-
Rozwój materiałów tytanowych na implanty aloplastyczne = Development of Ti-based materials for alloplastic implants
PublikacjaThe article is aimed at demonstraiting the previous results and current research work in the area made by Advanced Biomaterials Research Group at the Faculty of Mechanical Engineering. The paper concentrated on the developement of Ti-based biomaterials with improved biocompatibility and bioactivity.
Rok 2009
-
Modyfikacja struktury i właściwości warstwy wierzchniej stopu tytanu Ti-6Al-4V otrzymywanej metod,a nadtapiania laserowego w warunkach ultraszybkiej krystalizacji
PublikacjaPokazano wyniki badań wpływu nadtapiania laserowego przy zastosowaniu różnej mocy lasera na grubość i mikrostrukturę warstwy wierzchniej oraz zużycie tribokorozyjne w roztworze Ringera. Wykazano, że nadtapianie, choć powoduje powierzchniowe spękanie, prowadzi do znacznego wzrostu odporności na zużycie tribokorozyjne. Przyczyną jest znaczny wzrost twardości materiału przy równoczesnym zacieraniu pęknięć.
Rok 2008
-
Chapter 14 : A new concept of highly porous bioactive titanium alloys with hydroxyapatite coatings
PublikacjaPrzedstawiono koncepcję biomateriału o wysokiej bioaktywności i odporności na korozję. Omówiono metody wytwarzania porowatych stopów tytanu, techniki utleniania, techniki nakładania porowatego hydroksyapatytu, nakładanie bioaktywnych polimerów, metody badan i modelowania struktur porowatych.
-
Coatings in arthroplasty [online]
PublikacjaThe modern coatings used in arthroplasty for long term implants are reviewed. The phosphate coatingsare the most popular technique to improve the bone-implant interfacial strength and promote theosseointegration. The plasma spraying, electrophoretic precipitation, powder metallurgy, ion beamsputtering, high velocity oxy-fuel (HVOF) combustion spraying, sol-gel technique, biomimeticdeposition are mostly used to obtain the phosphate,...
-
Corrosion of titanium biomaterials, mechanisms, effects and modelisation
PublikacjaBadania in vivo oraz in vitro wskazują na bardzo małą szybkość korozji biostopów tytanu.Najczęstsza przycyną jest korozja ogólna i lokalna oraz korozja frettingowa. Trzy możliwe mechanizmy to: rozpuszczanie warstwy tlenku tytanu, dyfuzja pierwiastków przez warstwę tlenkową oraz reakcje elektrochemiczna w środowisku korozyjnym odsłoniętego metalu. Procesy korozyjne prowadzą do obluzowania implantów i poważnych schorzeń. Standardowe...