We report a successful synthesis of a high-purity intermetallic germanide Y2Pd1.25Ge2.75, crystallizing in the disordered variant of the AlB2-type structure. A single-phase sample was obtained via arc-melting by deliberately tuning the composition out of the ideal 2:1:3 ratio. Specific heat, electrical resistivity and magnetization measurements show that the compound is a weakly-coupled (λ e-p = 0.58) type-II superconductor with...

Single crystals of completely ordered variant of the YNi3Al9 compound were grown by self-flux method with excess of aluminum. The crystal structure of the title compound was redetermined from single crystal X-ray diffraction data. The structure adopts ErNi3Al9 type, space group R32, parameters of the unit cell a ​= ​7.2838(2) Å, c ​= ​27.4004(8) Å. The growth of relatively large single crystals of the YNi3Al9 compound, having completely...