Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses

Opis

Linear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO₂, 25% PbO, 15% Fe₂O₃ and 15% one of alkaline oxides: Na₂O, K₂O, Li₂O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in alumina crucibles. The melting of glass containing lithium ions was conducted in air at 1373K. The glasses with potassium ions and sodium ions were melted at 1473K. The melts were poured out on plate heated up to 673K and formed into small circular-shaped pellets (about 1,5 mm thick and 20 mm in diameter). Next glasses were annealing at the 673K and cooling with furnance. After a polishing, golden electrodes were evaporated at both sides of preheated samples in vacuum, for the electrical conductivity measurements. The linear and nonlinear impedance spectra were measured in the frequency range of 1 mHz to 1 MHz and in the temperature range of 153K to 483K by Concept 40 broadband dielectric spectrometer. The nonlinear electrical properties were measured also as a function of A.C. voltage in range of 0.01 - 1 Vrms.

Plik z danymi badawczymi

set2.zip

813.5 kB, S3 ETag 6dda09337b97a88e4206e454fdcb8cc8-1, pobrań: 60

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2012

Data zatwierdzenia:

2021-05-05

Data wytworzenia:

2011

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/2kp1-jf88

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 130 razy

Wyszukiwarka