Linear impedance of V2O5 nanorods obtained at 903K

Opis

The DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter and 1mm in thickness) under a compacting pressure of 25 kN/cm2. The V2O5 nanorods are achieved by annealing the pellet at 903K for 10 h with a heating rate of 0.1 K/min and a cooling rate of 0.5K/min.

For the electrical measurements, gold electrodes were evaporated at the preheated and ground sample. Impedance measurements were carried out in the temperature range from 153 K to 423 K, in the frequency range from 10mHz to 10 MHz, and with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.

Plik z danymi badawczymi

V2O5Nanorods2.zip

31.8 kB, S3 ETag 44ac75282761aad948ff7282cbf9fb82-1, pobrań: 52

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-07-13

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/7bzv-6352

Seria:

Vanadium oxides

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method

Cytuj jako

Autorzy

wyświetlono 103 razy

Wyszukiwarka