The linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass plate and pressed by another plate to obtain flat circular pellets of 1–2 mm thickness and 10–20 mm in diameter. Next subset of as-quenched samples was heat treated in air at the temperature of 633 K (close to the crystallization temperature) for 6 h and cooled with the furnace. For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and the temperature range from 153 K to 423 K, with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.
Detailed information you can find in: http://dx.doi.org/10.1016/j.jnoncrysol.2014.01.008
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2014
- Data zatwierdzenia:
- 2021-05-23
- Data wytworzenia:
- 2013
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/f982-x066 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
Cytuj jako
Autorzy
wyświetlono 43 razy