SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Opis
This Data set include SEM and EDX results of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous, and crystallised upon heat treatment at 500 ◦C. Microstructural analyses proved a homogeneous elemental distribution and the desired Fd-3 m cubic spinel structure. Electrical conductivity measurements indicated a dependence on the processing temperature, with the highest electrical conductivity values (~3 S cm 1 at 700 ◦C) obtained for layers heat-treated at 700 ◦C. The spray pyrolysis technique seems to be well suited to fabricating and exploring spinel-based high-entropy oxides synthesized as thin films, and to studying new compositions containing transition metal cations.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BY-NC-NDUżycie niekomercyjne - Bez utworów zależnych - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2023
- Data zatwierdzenia:
- 2023-08-04
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/08v6-dw78 otwiera się w nowej karcie
- Finansowanie:
- Seria:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
Cytuj jako
Autorzy
wyświetlono 132 razy