The dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
MAX matrice Mo3AlC2 was purchased from Luoyang Tongrun Info Technology, China.
MXene material was prepared via selective etching of aluminium using hydrofluoric acid (50%) for 96 h at room temperature. After the etching, the powders were flirted and washed with water and ethanol until pH reached 6. Then, the MXene was dried under vacuum at 50˚C for 24 h.
Nickel catalyst was prepared via impregnation of previously prepared Mo2CTx/Mo2AlC2 with aqueous nickel nitrate solution and drying at 50 deg. C under vacuum.
Catalytic process parameters:
- composition of intel stream: methane:carbon dioxide = 1:1
- temperature - 800 deg. C
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2022
- Data zatwierdzenia:
- 2022-09-20
- Data wytworzenia:
- 2021
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)
- inżynieria chemiczna (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/f7ev-an77 otwiera się w nowej karcie
- Finansowanie:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
- dane badawcze XRD data of V2AlC, Mo3AlC2, Mo3CTx and V2AlCTx
- dane badawcze SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
- dane badawcze Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Cytuj jako
Autorzy
wyświetlono 154 razy