The morphology of lead-borate glasses and nanocomposites doped with iron oxide

Opis

The topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional melt
quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and pressed by an another plate to obtain flat
circular samples of 1–2 mm thickness and 20–30 mm in diameter. The quenched pellets were annealed at the temperature of 673 K for 3 h and cooled with the furnace. The microstructure of all samples was determined by means of atomic forcemicroscopy at their fresh fractureswith the use of NT-MDT Ntegra AFM. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2014.01.042

Plik z danymi badawczymi

set9.zip

89.4 MB, S3 ETag 43f7abf082bc477b3342a5b58c9f0d5f-1, pobrań: 64

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-05

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/hcwb-e504

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Electrical properties and structure of lead-borate glass containing iron ions

Cytuj jako

Autorzy

wyświetlono 110 razy

Wyszukiwarka