The topography of Bi2VO5.5 ceramics prepared by melt-quenching technique was measured with confocal microscope
Opis
The topography of Bi2VO5.5 ceramics prepared by melt-quenching technique was measured by confocal microscope.
Two samples were prepared by the conventional melt quenching technique. First one was prepared from powdered ceramic Bi2VO5.5 (name:BiVas quenched ceramic), and the second one from appropriate amounts of Bi2O3 and V2O5 powders (name: BiVas quenched powders). The melting was conducted in alumina crucibles at 1173 K for few minutes. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks.
Additionally, melted samples were heat treated at 650 degC for 1h (BiVas quenched ceramic/powder crystallized).
The topography of the samples was also investigated by Confocal Microscope Olympus OLS 4000 Lext with a CCD camera.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2017
- Data zatwierdzenia:
- 2021-05-25
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/h0g2-2x73 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
- publikacja Nonlinear and linear impedance of bismuth vanadate ceramics and its relation to structural properties
- publikacja STRUKTURA ORAZ WŁAŚCIWOŚCI ELEKTRYCZNE MATERIAŁÓW SZKLISTYCH ZAWIERAJĄCYCH GRANULE FERROELEKTRYKA Bi2VO5,5
Cytuj jako
Autorzy
wyświetlono 108 razy