The topography of carbon black-polylactide composite 3D printed electrodes after femtosecond laser ablation

Opis

This dataset contains a series of scanning electron microscopy images revealing the topography of 3D printed carbon black-polylactide composite electrodes after laser ablation with a femtosecond laser. Different laser powers were investigated, namely: 10%, 25%, 50%, 75% and 100%. The CB-PLA electrodes were 3D printed using an Ender printer. Femtosecond laser NKT Photonics, Origami XP parameters: power at 100% - 200kHz, scan speed – 2500mm/s, air atmosphere The topography analysis was investigated by scanning electron microscopy (FEI Quanta FEG 250) with an Everhart–Thornley secondary electron detector at an acceleration voltage of 10 kV.

Plik z danymi badawczymi

PLA_femto.zip

135.0 MB, S3 ETag 369155354e7ebddcc7b2606ae4420567-1, pobrań: 73

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2022-07-29

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/d7f7-2f71

Finansowanie:

Technologia addytywnego wytwarzania elektroaktywnych przestrzennych struktur z kompozytów polilaktydu wzmacnianego diamentem

Seria:

Additive manufacturing technology of electroactive three-dimensional structures from diamond reinforced polylactide composites

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

dane badawcze Partial PLA composite surface activation by femtosecond laser ablation

Cytuj jako

Autorzy

wyświetlono 187 razy

Wyszukiwarka