The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation

Opis

The dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.

- CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged and washed several times. The powders were calcined at 400oC. Powders were single-phase.

- Ni(NO3)2*6H2O 1M solution was used for Ni introduction (beta-cyclodextrin was added for better metal dispersion)

Plik z danymi badawczymi

CLO20_10%Ni_CTAB_XRD.ASC

172.7 kB, S3 ETag 04b197d021e8fbeb17ef76bd179e3a9c-1, pobrań: 8

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC

Użycie niekomercyjne
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-06-10

Data wytworzenia:

2020

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/zcd7-ny52

Finansowanie:

Anodowe materiały katalityczne dla tlenkowych ogniw paliwowych bezpośrednio zasilanych biogazem (DIR-SOFCs)

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

dane badawcze The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method

Cytuj jako

Autorzy

wyświetlono 44 razy

Wyszukiwarka