Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere

Opis

The DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.

Thermogravimetric analysis (TG) and Differential scanning calorimetry (DSC) measurements were carried out under synthetic air atmosphere from 35°C to 650°C (with a heating rate of 15 °C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum (MS). The gases that come out from the samples during heating were monitored by the quadruple mass spectrometer Netzsch QMS 403C Aeolos. The mass spectra were measured for selected m/z from 12 to 44.

Plik z danymi badawczymi

Xero500Ar.zip

167.7 kB, S3 ETag a61949879cff67a5fd938b024aea0159-1, pobrań: 47

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-07-13

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/5n76-6m72

Seria:

Vanadium oxides

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method

Cytuj jako

Autorzy

wyświetlono 105 razy

Wyszukiwarka