Abstrakt
This paper shows results of weldability testing of fine-grained high -strength low- alloy S460N steel welded in water environment by covered electrodes. The tests were carried out by using the CTS test specimens with fillet welds. Four specimens were welded under water and one specimen in air. Welded joints were subjected to non-destructive visual and penetration tests. The accepted joints were then subjected to macroscopic and microscopic inspection and Vickers hardness measurements as well. The experiments showed that S460N steel welded in water environment is characterized by a high susceptibility to cold cracking.
Cytowania
-
2 7
CrossRef
-
0
Web of Science
-
2 7
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pobierz publikację
pobrano 71 razy
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/pomr-2018-0104
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
Polish Maritime Research
nr 25,
wydanie 3 (99),
strony 131 - 136,
ISSN: 1233-2585 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Tomków J., Łabanowski J., Fydrych D., Rogalski G.: COLD CRACKING OF S460N STEEL WELDED IN WATER ENVIRONMENT// Polish Maritime Research. -Vol. 25, iss. 3 (99) (2018), s.131-136
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/pomr-2018-0104
- Źródła finansowania:
-
- Działalność statutowa/subwencja
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 181 razy