Fabrication of Bi6Fe2Ti3O18 Ceramics by Mixed Oxide Method

Agata Lisińska-Czekaj

doi:10.4028/www.scientific.net/msf.730-732.100

Fabrication of Bi6Fe2Ti3O18 Ceramics by Mixed Oxide Method

Abstrakt

In the present study Bi6Fe2Ti3O18 (BFTO) ceramics has been fabricated by solid state reaction from the mixture of simple oxides viz. Bi2O3, TiO2 and Fe2O3. Stoichiometric mixture of the powders was thermally analyzed so parameters of the thermal treatment were determined. The EDS measurements have shown conservation of the chemical composition of the ceramic powder after calcination. Hot-pressing method was used for final densification of ceramic samples. The crystalline structure of the sintered samples was examined by X-ray diffraction method at room temperature. It was found that BFTO ceramics sintered at T=980 °C adopted the orthorhombic structure of Aba2 (41) space group with the following elementary cell parameters: a=5.4567(2)Å, b=49.418(2) and c=5.4826(2). Details concerning the atom’s positions are presented.

Cytowania

0

CrossRef
0

Web of Science
3

Scopus

Autor (1)

Agata Lisińska-Czekaj dr hab.

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

pełna treść artykułu zobacz w serwisie zewnętrznym otwiera się w nowej karcie

Słowa kluczowe

BISMUTH LAYER-STRUCTURED CERAMICS, CERAMIC, CRYSTAL STRUCTURE, MIXED OXIDE METHOD

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuły w czasopismach
Opublikowano w:: MATERIALS SCIENCE FORUM strony 100 - 104,
ISSN: 0255-5476
Język:: angielski
Rok wydania:: 2012
Opis bibliograficzny:: Lisińska-Czekaj A.: Fabrication of Bi6Fe2Ti3O18 Ceramics by Mixed Oxide Method// MATERIALS SCIENCE FORUM -,iss. 730-732 (2012), s.100-104
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.4028/www.scientific.net/msf.730-732.100
Weryfikacja:: Politechnika Gdańska