Abstrakt
Bismuth niobate (BiNbO4) ceramics were fabricated by mixed oxide method and sintered by presureless sintering method. BiNbO4 ceramics doped with V2O5 additive in amount 0.125 wt%, 0.250 wt% and 1 wt% of was sintered at T = 910°C whereas BiNbO4 ceramics doped with 2 wt% of CuO additive was sintered at T = 890°C and T = 910°C. It was found that V2O5 additive improved morphology of the ceramic samples. However, the chemical composition of BiNbO4 ceramics in relation to bismuth oxide and niobium oxide manifested a tendency of lack of Bi2O3 component. Absorption bands for the BiNbO4 compound were identified. FTIR band positions associated with NbO6 octahedra suggested that the crystal structure changes after V2O5 incorporation.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (3)
-
Iwona Kuźniarska-Biernacka dr hab.
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.24425/amm.2020.132826
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
ARCHIVES OF METALLURGY AND MATERIALS
nr 65,
strony 817 - 821,
ISSN: 1733-3490 - Język:
- angielski
- Rok wydania:
- 2020
- Opis bibliograficzny:
- Kuźniarska-Biernacka I., Lisińska-Czekaj A., Czekaj D.: STUDY OF CuO AND V2O5 EFFECT ON IR SPECTRA OF POLYCRYSTALLINE BISMUTH NIOBATE// ARCHIVES OF METALLURGY AND MATERIALS -Vol. 65,iss. 2 (2020), s.817-821
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.24425/amm.2020.132826
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 122 razy
Publikacje, które mogą cię zainteresować
Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics
- A. Lisińska-Czekaj,
- D. Czekaj,
- K. Osińska
- + 1 autorów