High temperature corrosion of evaporator tubes with thermal sprayed coatings

Abstrakt

Degradation examinations of outer surface of low-emission steam boiler evaporator tubes are presented in the paper. Metallographic evaluation of scale morphology, its micro sites chemical composition analysis and distribution of elements on cross sections have been performed. Water-wall tubes were exposed in steam boiler for up to two years period. Common tubes made of 16Mo3 steel suffered sulphide and molten salts corrosions. Thermal sprayed tubes with the single layer of 70%Ni 30%Cr alloy show better corrosion resistance, but become also susceptible to sulphide corrosion due to presence of internal voids and cracks. Double layer Al2O3/Ni-30Cr coatings withstand corrosion attack for more than one year operation, and then failed due to internal heterogeneity and cracks generation.

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Solid State Phenomena nr 165, strony 110 - 117,
ISSN: 1012-0394
Język:
angielski
Rok wydania:
2010
Opis bibliograficzny:
Łabanowski J., Ćwiek J.: High temperature corrosion of evaporator tubes with thermal sprayed coatings// Solid State Phenomena. -Vol. 165., (2010), s.110-117
Weryfikacja:
Politechnika Gdańska

wyświetlono 76 razy

Publikacje, które mogą cię zainteresować

Meta Tagi