Instantaneous impedance monitoring of synergistic effect between cavitation erosion and corrosion processes
Abstrakt
The most common method of determination of cavitation erosion resistance as well as the magnitude of erosion-corrosion synergistic interaction is based on the weight loss measurements. Nondestructive characterization of installations elements is in most cases impossible to perform. Also, such a measurement does not include local types of failure or alteration of operating conditions. There is an urge to elaborate a method for monitoring of cavitation erosion-corrosion damage. The authors used dynamic impedance technique to study change of electric parameters of various engineering alloys under synergistic interaction of cavitation erosion and corrosion in 3% NaCl solution. Monitoring of electric parameters offers a very good resemblance to failure level identified with weight loss function and microscopic analysis. It was possible to distinguish different stages of material degradation by means of instantaneous impedance measurements. Instantaneous value of charge transfer resistance provides information about synergistic influence of mechanical erosion on corrosion.
Cytowania
-
3 9
CrossRef
-
0
Web of Science
-
3 9
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
ELECTROCHIMICA ACTA
nr 203,
strony 388 - 395,
ISSN: 0013-4686 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Ryl J., Wysocka J., Ślepski P., Darowicki K.: Instantaneous impedance monitoring of synergistic effect between cavitation erosion and corrosion processes// ELECTROCHIMICA ACTA. -Vol. 203, (2016), s.388-395
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.electacta.2016.01.216
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
wyświetlono 150 razy