Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal
Abstrakt
One of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state of the art of considered issues was described and results of preliminary investigations were presented. The level of diffusible hydrogen was determined by a glycerin test. Five factors were considered: the flow rate of shielding gas, the welding current, the arc voltage, the welding speed and the electrode stickout. All factors were optimized using a Plackett-Burman design to get the most relevant variables. The results of the experiment indicate that appropriate choice of welding parameters may reduce diffusible hydrogen content in deposited metal.
Autorzy (3)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Aktywność konferencyjna
- Typ:
- publikacja w wydawnictwie zbiorowym recenzowanym (także w materiałach konferencyjnych)
- Tytuł wydania:
- XXI International Symposium Research-Education-Technology strony 1 - 4
- Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Świerczyńska A., Tomków J., Fydrych D.: Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal// XXI International Symposium Research-Education-Technology/ Gdańsk: Gdańsk University of Technology Faculty of Mechanical Enginering, 2013, s.1-4
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 120 razy