Quasistatic and fatigue behavior of an AISI H13 steel obtained by additive manufacturing and conventional method
Abstrakt
This work aims to compare the mechanical behavior of an AISI H13 steel obtained by additive manufacturing with that obtained by conventional manufacturing methods. The average values of the ultimate tensile strength (UTS) and ductility obtained for the specimens produced by the conventional method were equal to 658 MPa and 18%, respectively, which compares with 503 MPa and 0.75% registered for the selective laser melting (SLM) specimens. Inversely, the average hardness value determined for the SLM specimens was higher, 450 HV, than the observed for the conventional, 200 HV. In addition, the maximum applied stress corresponding to a fatigue limit's endurance of 2 x 106 cycles was equal to 340 and 85 MPa for conventional and SLM specimens, respectively. Therefore, from a fatigue design point of view, it was possible to infer that σmax/UTS = 0.17 for the SLM specimens tested. Porosity and lack of fusion influenced the static and the fatigue strength negatively in the SLM specimens.
Cytowania
-
2 1
CrossRef
-
0
Web of Science
-
2 4
Scopus
Autorzy (7)
-
José F. Garcias
-
Rui F. Martins
-
Ricardo Branco
-
Zbigniew Marciniak
-
Cândida Pereira
-
Cyril Santos
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1111/ffe.13565
- Licencja
- Copyright (2021 John Wiley & Sons, Ltd)
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
nr 44,
strony 3384 - 3398,
ISSN: 8756-758X - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Garcias J. F., Martins R. F., Branco R., Marciniak Z., Macek W., Pereira C., Santos C.: Quasistatic and fatigue behavior of an AISI H13 steel obtained by additive manufacturing and conventional method// FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES -Vol. 44,iss. 12 (2021), s.3384-3398
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1111/ffe.13565
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 60 razy
Publikacje, które mogą cię zainteresować
Fatigue fracture morphology of AISI H13 steel obtained by additive manufacturing
- W. Macek,
- R. F. Martins,
- R. Branco
- + 3 autorów
Selective Laser Melting of Ti Alloy for Manufacturing The Prosthetic Elements
- T. Seramak,
- K. Zasińska,
- J. Andryskowski
- + 3 autorów
Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel
- R. Branco,
- J. D. Costa,
- J. A. M. Ferreira
- + 3 autorów