Abstrakt
The influence of high-temperature reduction/oxidation treatment on the structural properties of superconducting PrBa2Cu3O7−δ (PrBCO) single crystals was examined. The scanning electron microscopy (SEM) analysis has shown that even the short-lasting exposure to the oxygen-deficient atmosphere leads to creation of regular-shaped crystallites of PrBaO3 and BaCuO2 phases with the size of 0.5 ÷ 2.0 μm on the smooth and flat crystal surface. The energy dispersive x-ray (EDX) investigations performed on the cross-sections of the superconducting crystals have indicated that the post-growth thermal treatment reduces the amount of Pr on the Ba-sites. Our results strongly support all the concepts attributing the suppression of superconductivity in this system to the excess of Pr in the crystal structure of samples synthesised by the standard methods.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (4)
-
Jan Olchowik
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- Publikacja w czasopiśmie
- Rok wydania:
- 2000
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/s0921-4534(00)00573-6
- Weryfikacja:
- Brak weryfikacji
wyświetlono 14 razy
Publikacje, które mogą cię zainteresować
Growth, Crystal Structure and Magnetic Characterization of Zn-Stabilized CePtIn4
- E. M. Carnicom,
- T. Klimczuk,
- F. v. Rohr
- + 6 autorów
MgPd2Sb : A Mg-based Heusler-type superconductor
- M. Winiarski,
- G. Kuderowicz,
- K. Górnicka
- + 5 autorów