Abstrakt
In the present paper studies on Bi1xNdxFeO3 for x =0.1-0.4 are reported. The mixed oxide method followed with pressureless sintering was employed for ceramics fabrication. Thermal behavior of stoichiometric mixtures of simple oxide powders, viz. Bi2O3, Nd2O3 and Fe2O3 was studied by simultaneous thermal analysis. It was found that with an increase in neodymium content the weight loss increased from 0.75% to 3.16% for x =0.1 and x =0.4, respectively. It was found that weight loss took place mainly within two temperature ranges, namely T1 (300-400)0C and T2 (600-800)0C. Bi1xNdxFeO3 ceramics was studied in terms of its phase composition (X-ray phase analysis) and chemical composition (EDS method) at room temperature. It was found that Bi1xNdxFeO3 suffered structural phase transition from rhombohedral to orthorhombic symmetry with an increase in neodymium concentration x within the range x =(0.2-0.3).
Cytowania
-
1 3
CrossRef
-
0
Web of Science
-
1 0
Scopus
Autorzy (4)
-
Jolanta Dzik dr
-
Aldona Zarycka dr
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/amm-2013-0177
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
ARCHIVES OF METALLURGY AND MATERIALS
nr 58,
strony 1371 - 1376,
ISSN: 1733-3490 - Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Dzik J., Lisińska-Czekaj A., Zarycka A., Czekaj D.: Study of Phase and Chemical Composition of Bi1-xNdxFeO3 Powders Derived by Pressureless Sintering// ARCHIVES OF METALLURGY AND MATERIALS -Vol. 58,iss. 4 (2013), s.1371-1376
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/amm-2013-0177
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 116 razy
Publikacje, które mogą cię zainteresować
Mg2+ Doping Effects on the Structural and Dielectric Properties of CaCu3Ti4O12 Ceramics Obtained by Mechanochemical Synthesis
- P. Dulian,
- W. Bąk,
- M. Piz
- + 5 autorów
Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics
- A. Lisińska-Czekaj,
- D. Czekaj,
- K. Osińska
- + 1 autorów
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
- A. Lisińska-Czekaj,
- D. Czekaj,
- B. Garbarz
- + 2 autorów