Thin layer of ordered boron-doped TiO2 nanotubes fabricated in a novel type of electrolyte and characterized by remarkably improved photoactivity
Abstrakt
This paper reports a novel method of boron doped titania nanotube arrays preparation by electrochemical anodization in electrolyte containing boron precursor – boron trifluoride diethyl etherate (BF3 C4H10O), simultaneously acting as an anodizing agent. A pure, ordered TiO2 nanotubes array, as a reference sample, was also prepared in solution containing a standard etching compound: ammonium fluoride. The doped and pure titania were characterized by scanning electron microscopy, UV–vis spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, photoluminescence emission spectroscopy and by means of electrochemical methods. The B-doping decidedly shifts the absorption edge of TiO2 nanotubes towards the visible light region and significantly inhibits the radiative recombination processes. Despite the fact that the doped sample is characterized by 4.6 lower real surface area when compared to pure titania, it leads to the decomposition of methylene blue in 93%, that is over 2.3 times higher than the degradation efficiency exhibited by the undoped material. The formation rate of hydroxyl radicals (•OH) upon illumination significantly favours boron doped titania as a photocatalytic material. Moreover, the simple doping of TiO2 nanotubes array results in the enhancement of generated photocurrent from 120 A/cm2 to 350 A/cm2 registered for undoped and doped electrode, respectively.
Cytowania
-
4 6
CrossRef
-
0
Web of Science
-
4 4
Scopus
Autorzy (6)
-
-
Katarzyna Grochowska
- Instytut Maszyn Przepływowych Inżynierii Plasmowej i Laserowej
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
APPLIED SURFACE SCIENCE
nr 357,
strony 942 - 950,
ISSN: 0169-4332 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Siuzdak K., Szkoda M., Lisowska-Oleksiak A., Grochowska K., Karczewski J., Ryl J.: Thin layer of ordered boron-doped TiO2 nanotubes fabricated in a novel type of electrolyte and characterized by remarkably improved photoactivity// APPLIED SURFACE SCIENCE. -Vol. 357, nr. Part A (2015), s.942-950
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.apsusc.2015.09.130
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 191 razy
Publikacje, które mogą cię zainteresować
Enhanced capacitance of composite TiO2 nanotube / boron-doped diamond electrodes studied by impedance spectroscopy
- K. Siuzdak,
- M. Sawczak,
- R. Bogdanowicz
- + 1 autorów