Three-Dimensional Fractography for Conventional and Additive Manufactured Steels After Bending-Torsion Fatigue
Abstrakt
In this study, fracture surface topography parameters were measured to investigate the effects of multiaxial loading. In order to assess the metrological aspects of fracture for notched specimens made of high-strength steels processed by both conventional and additively manufacturing (AM) techniques, an optical surface profilometer was used. Three bending moment to torsion moment ratios (B/T) were studied, i.e. 2, 1 and 2/3. The geometries were solid round bars with lateral notches made of conventional steel and hollow round bars with transversal holes for AM specimens. The investigations indicate that arithmetical mean height, Sa, decreased and fractal dimension, Df, increased with higher B/T ratios and higher fatigue lives.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Ricardo Branco
-
Jarosław Trembacz
-
José Domingos Costa
-
J. A. M. Ferreira
-
Carlos Capela
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja monograficzna
- Typ:
- rozdział, artykuł w książce - dziele zbiorowym /podręczniku w języku o zasięgu międzynarodowym
- Opublikowano w:
-
Structural Integrity
nr 25,
strony 127 - 135,
ISSN: 2522-560X - Tytuł wydania:
- Structural Integrity and Fatigue Failure Analysis strony 127 - 135
- Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Macek W., Branco R., Trembacz J., Costa J. D., Ferreira J. A. M., Capela C.: Three-Dimensional Fractography for Conventional and Additive Manufactured Steels After Bending-Torsion Fatigue// Structural Integrity and Fatigue Failure Analysis/ : , 2022, s.127-135
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/978-3-030-91847-7_13
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 57 razy
Publikacje, które mogą cię zainteresować
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 autorów
Fatigue fracture surface metrology of thin-walled tubular austenitic steel specimens after asynchronous loadings
- W. Macek,
- Ł. Pejkowski,
- R. Branco
- + 2 autorów
Fractographical quantitative analysis of EN-AW 2024 aluminum alloy after creep pre-strain and LCF loading
- W. Macek,
- A. Tomczyk,
- R. Branco
- + 2 autorów
Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load
- W. Macek,
- D. Rozumek,
- S. Faszynka
- + 3 autorów