Tribological Properties of Ni-P/Si3N4 Nanocomposite Layers Deposited by Chemical Reduction Method on Aluminum Alloy AW-7075

Abstrakt

The article presents the results of tribological tests of Ni-P/Si3N4 nanocomposite and Ni-P nickel layers deposited on the AW-7075 aluminum alloy by chemical reduction method, and the AW-7075 alloy without coating. Nanocomposite layers were produced using Si3N4 siliconnitride in the form of a polydisperse powder whose particle sizes ranged from 20 to 25 nm. The influence of the content of the dispersion phase layer material on the abrasive wear, which was determined as the “ball on disc” method, was analyzed. Surface topography was examined by the contact method using a profilometer. The purpose of introducing Si3N4 particles into the Ni-P layer was to increase the wear resistance of AW-7075 aluminum alloy parts with an embedded nanocomposite coating. Based on the obtained test results, it was found that the Ni-P/Si3N4 layers are more resistant to wear than the Ni-P layers and the AW-7075 alloy layers, and are a good barrier against abrasive wear at various loads and environmental conditions.

Cytowania

  • 1

    CrossRef

  • 1

    Web of Science

  • 1

    Scopus

Cytuj jako

Pełna treść

pobierz publikację
pobrano 0 razy
Wersja publikacji
Accepted albo Published Version
Licencja
Creative Commons: CC-BY otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
Materials nr 13,
ISSN: 1996-1944
Język:
angielski
Rok wydania:
2020
Opis bibliograficzny:
Czapczyk K.: Tribological Properties of Ni-P/Si3N4 Nanocomposite Layers Deposited by Chemical Reduction Method on Aluminum Alloy AW-7075// Materials -Vol. 13,iss. 24 (2020), s.5797-
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma13245797
Weryfikacja:
Politechnika Gdańska

wyświetlono 13 razy

Publikacje, które mogą cię zainteresować

Meta Tagi