Abstrakt
A series of Er3+-TiO2, Yb3+-TiO2 and Er3+/Yb3+-TiO2 photocatalysts were obtained via sol-gel method, using rare earth metal (RE) precursor ranging from 0.25 to 10 mol%. The experiments demonstrated that phenol in aqueous solutions was successfully degraded under visible light (> 450 nm) using RE3+-TiO2. The as-prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron emission spectroscopy (XPS), UV-Vis absorption measurement, BET surface area analysis and luminescent spectroscopy. XPS analysis revealed that erbium and ytterbium were present in the form of oxides. The sample showing the highest photoactivity was in the form of anatase, its surface area equaled to 125 m2/g, average crystals size was 13 nm and contained 1 mol% of Yb3+. 3 h of irradiation resulted in 89 % of phenol degradation under visible light. For TiO2 materials doped with Er3+ or Yb3+/Er3+ after excitation by 978 nm laser beam, low intensive up-conversion emission was observed. Action spectra analysis of Er/Yb-TiO2 revealed that irradiation from range 420 to 475 nm is responsible for visible light photocatalytic activity.
Autorzy (7)
-
Tomasz Grzyb
- Uniwersytet Adama Mickiewicza w Poznaniu Zakład Ziem Rzadkich
-
Janusz W. Sobczak
- Polska Akademia Nauk w Warszawie Instytut Chemii Fizycznej
-
Wojciech Lisowski
- Polska Akademia Nauk w Warszawie Instytut Chemii Fizycznej
-
Bunsho Ohtani
- Hokkaido University Catalysis Research Center
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
APPLIED CATALYSIS B-ENVIRONMENTAL
nr 163,
strony 40 - 49,
ISSN: 0926-3373 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Reszczyńska J., Grzyb T., Sobczak J., Lisowski W., Gazda M., Ohtani B., Zaleska-Medynska A.: Visible light activity of rare earth metal doped (Er3+, Yb3+ or Er3+/Yb3+) titania photocatalysts// APPLIED CATALYSIS B-ENVIRONMENTAL. -Vol. 163, (2015), s.40-49
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 143 razy
Publikacje, które mogą cię zainteresować
Preparation and photocatalytic activity of Nd-modified TiO2 photocatalysts: Insight into the excitation mechanism under visible light
- P. Parnicka,
- P. Mazierski,
- T. Grzyb
- + 6 autorów
Lanthanide co-doped TiO2: the effect of metal type and amount on surface properties and photocatalytic activity
- J. Reszczyńska,
- T. Grzyb,
- J. W. Sobczak
- + 4 autorów
Studies on novel BiyXz-TiO2/SrTiO3 composites: Surface properties and visible light-driven photoactivity
- M. Marchelek,
- E. Grabowska,
- T. Klimczuk
- + 3 autorów