SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ
Dane BadawczeThis dataset contains results of the research on the basis of which the Figures presented in the manuscript entitled "Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ on structural, electrical, and electrochemical properties for potential oxygen electrode of intermediate temperature Solid Oxide Cells" were prepared. A detailed description...
-
The hydrogen evolution reaction (HER) performance of some FTO/MoS2/SnO2 electrodes
Dane BadawczeTo demonstrate the electrochemical performance of the FTO/MoS2/SnO2 for HER (hydrogen evolution reaction), the LSV (linear sweep voltammetry) was performed. The polarization curves of the obtained composite were measured in 1 M H2SO4 at room temperature with a scan rate 10 mV/s. For comparison, the LSV for the FTO, pure MoS2 and Pt plate electrode were...
-
A set of data constituting the basis for the publication entitled "Mitochondria dysfunction is one of the causes of diclofenac toxicity in the green alga Chlamydomonas reinhardtii"
Dane BadawczeNon-steroidal anti-inflammatory drugs (NSAIDs), such as diclofenac (DCF), form a significant group of environmental contaminants. When the toxic effects of DCF on plants are analyzed, authors often focus on photosynthesis, whilemitochondrial respiration is usually overlooked. Therefore, an in vivo investigation of plant mitochondria functioning under...
-
Depth chemical profile in a CeIr3 sample
Dane BadawczeThe polycrystalline sample of CeIr3 used in the present studies was synthesized by arc-melting cerium (4N) and iridium (3N5) in an arc furnace on a water-cooled copper hearth using a tungsten electrode under a high purity argon atmosphere. A piece of zirconium was used as an oxygen getter. First, a button of Ir was prepared by arc-melting the iridium...
-
Electrical conductivity of the Sr0.86Ti0.65Fe0.35O3-d pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense Sr0.86Ti0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method. Studies were performed at different oxygen partial pressures (20%, 1% and 0.1%) under humidified (~4 vol%) gas flow rate of 50 ml min -1.
-
SEM images of symmetrical cell interface with SrTi0.50Fe0.50O3-d electrode and CGO-20 substrate in function of sintering temperature
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.50Fe0.50O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
Electrical conductivity of the (Ce0.80Gd0.20)O1.90 pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense (Ce0.80Gd0.20)O1.90 (CGO-20) pellet. DC electrical conductivity measurements of CGO-20 were performed by the Van der Pauw method between 900 °C and 450 °C with 50 °C step. Studies were performed at different oxygen partial pressures (100%, 20% and 1%) under humidified (~4...
-
SEM image and EDS map of SrTi0.30Fe0.70O3-d powder aglomerate
Dane BadawczeThis dataset contains image of the SrTi0.30Fe0.70O3-d powder aglomerate with EDS map analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum mode. The chemical compositions of the investigated powder were determined...
-
SEM image and line EDS of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with line EDS analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 20 kV in a high vacuum mode. The chemical compositions of the investigated powder...
-
SEM images of symmetrical cell interface with SrTi0.30Fe0.70O3-d electrode and CGO-20 substrate in function of sintering temperature
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.30Fe0.70O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
SEM image and EDS map of SrTi0.50Fe0.50O3-d powder aglomerate
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d powder aglomerate with EDS map analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum mode. The chemical compositions of the investigated powder were determined...
-
SEM image and EDS map of SrTi0.65Fe0.35O3-d powder aglomerate
Dane BadawczeThis dataset contains image of the SrTi0.65Fe0.35O3-d powder aglomerate with EDS map analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum mode. The chemical compositions of the investigated powder were determined...
-
SEM images of symmetrical cell interface with SrTi0.65Fe0.35O3-d electrode and CGO-20 substrate in function of sintering temperature
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.65Fe0.35O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
SEM images of symmetrical cell interface with SrTi1-xFexO3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi1-xFexO3-d (x=0.35; 0.50; 0..70) electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum...
-
SEM image and EDS map of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with EDS map analysis results. This study were performed for better understanding the chemical composition of flat like structures that occurs in electrode. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope...
-
Electrical conductivity of the SrTi1-xFexO3-d pellets at 20% pO2
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense SrTi1-xFexO3-d (x=0.35, 0.50, 0.70) pellets. DC electrical conductivity measurements were performed by the Van der Pauw method between 900 °C and 200 °C. Studies were performed at 20% of oxygen partial pressure under humidified (~4 vol%) gas flow rate of 50 ml min -1.
-
SEM images of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
Thermogravimetric analysis (TGA) of the SrxTi0.30Fe0.70O3-d materials
Dane BadawczeThis dataset contains results of thermogravimetric analysis (TGA) fot SrxTi0.30Fe0.70O3-d materials (x=0.90, 0.95, 1.00 and 1.05). The TGA experiments were carried out using a microbalance (CI Precision MK5) in the temperature range between 900 °C and 200 °C. During the whole measurement procedure, air was fed to the furnace chamber at a flow rate of...
-
SEM images of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
Dilatometry results of SrxTi0.30Fe0.70O3-d materials
Dane BadawczeThis dataset contains results of dilatometry measurements of SrxTi0.30Fe0.70O3-d (x=0.90, 0.95, 1.00 and 1.05) materials. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrxTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for...
-
SEM images of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
Low temperature electrical conductivity of the SrFeO3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrFeO3-d (SFO) pellet. DC electrical conductivity measurements of SFO were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas flow rate of 40...
-
X-ray diffractometry results of the Sr1.05Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.05Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Low temperature electrical conductivity of the SrTi0.65Fe0.35O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.30Fe0.70O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.30Fe0.70O3-d (STF70) pellet. DC electrical conductivity measurements of STF70 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.50Fe0.50O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.50Fe0.50O3-d (STF50) pellet. DC electrical conductivity measurements of STF50 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
X-ray diffractometry results of the Sr0.90Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.90Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr1.00Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.00Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
Low temperature electrical conductivity of the SrTi0.10Fe0.90O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.10Fe0.90O3-d (STF90) pellet. DC electrical conductivity measurements of STF90 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
X-ray diffractometry results of the Sr0.95Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.95Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
Laser microscope profilometry of SrTi0.3Fe0.7O3-d electrode surface after quickly drying
Dane BadawczeThe dataset consists of a surface image, topography and profilometry obtained using a Keyence VK-X1000 confocal laser microscope for SrTi0.3Fe0.7O3-d electrode (STF70). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable...
-
Laser microscope profilometry of (Ce0.80Gd0.20)O1.90 surface before polishing
Dane BadawczeThe dataset consists of a surface image and topography obtained using a Keyence VK-X1000 confocal laser microscope for (Ce0.80Gd0.20)O1.90 substrate (CGO-20). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable focus. The...
-
Laser microscope profilometry of (Ce0.80Gd0.20)O1.90 after ∼3 μm surface finish
Dane BadawczeThe dataset consists of a surface image and topography obtained using a Keyence VK-X1000 confocal laser microscope for (Ce0.80Gd0.20)O1.90 substrate (CGO-20). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable focus. The...
-
Laser microscope profilometry of SrTi0.3Fe0.7O3-d electrode surface after slowly drying
Dane BadawczeThe dataset consists of a surface image, topography and profilometry obtained using a Keyence VK-X1000 confocal laser microscope for SrTi0.3Fe0.7O3-d electrode (STF70). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable...
-
X-ray diffractometry results of the Sr0.86Ti0.65Fe0.35O3 powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.86Ti0.65Fe0.35O3-d (STF35) powder. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. It confirms the formation of the cubic perovskite oxide phase. Calculated average lattice constant is a 3.90882(1) Å, with Goodness of Fit...