Wyniki wyszukiwania dla: impedance measurements
-
Impedance spectra of ZnO varistor type 440 model O ver. 68
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 10 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
Impedance spectra of ZnO varistor type 680 model O M ver. 65 60
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 10 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Fitted impedance spectra of a symmetrical porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C, measured at 700 °C and 0.1% pO2) with an individual contributions of the respective fitting elements
Dane BadawczeThis dataset contains exemplary impedance spectra (measured at 700 °C and 0.1% pO2) for porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode sintered at 1000 °C. Results of symmetric cell impedance measurement were converted to electrode surfaces area and dived by two electrodes. Dataset conatins also fitting results and individual contributions of the respective...
-
Fitted impedance spectra of a symmetrical porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C, measured at 800 °C and 0.1% pO2) with an individual contributions of the respective fitting elements
Dane BadawczeThis dataset contains exemplary impedance spectra (measured at 800 °C and 0.1% pO2) for porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode sintered at 1000 °C. Results of symmetric cell impedance measurement were converted to electrode surfaces area and dived by two electrodes. Dataset conatins also fitting results and individual contributions of the respective...
-
Dynamic impedance data for various carboxylic acids corrosion inhibition of aluminium in alkaline media (pH=11)
Dane BadawczeThis dataset contains the results of Dynamic Electrochemical Impedance Spectroscopy (DEIS) carried out in galvanostatic mode under iDC=0, carried out in order to define the corrosion inhibition effect of various studied carboxylic acids: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, carballylic acid, and serine. The experiment...
-
Impedance spectra of RC model as a result of testing pulse excitation measurement method
Dane BadawczeThe impedance spectrum of RC model object obtained using pulse excitation EIS impedance spectrosocpy measurement method. The 1V voltage pulse excitation duration was set to 0.1s and the total acqusition time was set to 1000s. The object under test was built using RC components connected as Baunier model of anticorrosion coating with the following components...
-
Model dynamic electrochemical impedance spectroscopy (DEIS) results obtained with various DC polarization rates
Dane BadawczeThe dataset contains results of model dynamic electrochemical impedance spectroscopy studies carried out on a setup of 10 diodes in series, which were connected in parallel with a condenser. The impedance data were acquired every 1 s (the analytic window length for Fourier Transform was 1 s). The model system was polarized between 0 and +8 V with DEIS...
-
The voltage across and current through the RC model object tested using pulse excitation in impedance spectroscopy measurement method
Dane BadawczeThe raw data (voltage across and current through RC model object ) obtained using pulse excitation EIS impedance spectroscopy measurement method. The data was acquired using 12-bit ADC (LTC1420) with sampling frequency changed in time segments. The 1V voltage pulse excitation duration was set to 0.1s and the total acqusition time was set to 1000s. For...
-
Electrochemical Impedance Spectroscopy data of PDA-modified TiO2 nanotubes
Dane BadawczeThis dataset contains Electrochemical Impedance Spectroscopy data of the samples from TiO2 nanotubes modified with polydopamine. The studies were presented as a part of the research on "Band Gap Engineering toward Semimetallic Character of Quinone-Rich Polydopamine" (DOI: 10.1021/acs.jpcc.2c08804).
-
Distribution of Relaxation Times analysis results of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C) as a function of measuring temperature at 0.1% pO2
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode as a function of measuring temperature at 0.1% pO2. Electrode was sintered at 1000 °C and measured at different temperatures (800 °C, 750 °C, 700 °C).
-
Carbonized Metal-Organic Frameworks-based strucutres with aluminium, phosphorus and nitrogen
Dane BadawczeThe dataset includes Raman spectra of carbonized Metal-Organic Frameworks (MOF) [acquired on Renishaw] and electrochemical properties of the materials [acquired on EC Lab], which includes techniques such as Linear Sweep Voltammetry (LCV), Electrochemical Impedance Spectroscopy (EIS), Taffel slope and Chronopotentiometry (CP).
-
Distribution of Relaxation Times analysis results of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C) as a function of oxygen partial pressure at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode as a function of oxygen partial pressure at 800 °C. Electrode was sintered at 1000 °C and measured at different oxygen partial pressures (10% pO2, 1% pO2, 0.1% pO2).
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Dane BadawczeLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.30Fe0.70O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.50Fe0.50O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
The electrochemical impedance spectroscopy studies of cataphoretic-grown epoxy-based coatings
Dane BadawczeThe dataset contains electrochemical impedance spectroscopy spectra collected for epoxy-based cataphoretic coatings in order to determine the offered anti-corrosion protection. Particular spectra pertain to the coatings applied for the different magnitude of polarization potential imposed, namely 10V, 20V and 30V. The results were obtained within the...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Oxygen partial pressure and temperature dependence of Gerischer element of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of Gericher element at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C)and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent circuit...
-
Oxygen partial pressure and temperature dependence of low frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of low frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of middle frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of low frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of low frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of series resistance (R) at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of middle frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element series resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Electrochemical studies for screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains electrochemical examination of SPCE paste and SPCE containing boron-doped diamond BDD foils. The studies include kinetics analyses with cyclic voltammetry and electrochemical impedance spectroscopy with different redox probes: hexacyanoferrate(III) and Hexaammineruthenium(III) and potentiostatic open circuit potential at different...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Morphological and electrochemical characterization of ceramic carbon foam electrodes water treatment applications
Dane BadawczeThis dataset contains morphological and electrochemical characterization of ceramic carbon foam employed as an electrode (CFFE) for the oxidation of a target pollutant. The dataset includes:
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...