Filtry
wszystkich: 6010
wybranych: 989
-
Katalog
- Publikacje 3854 wyników po odfiltrowaniu
- Czasopisma 137 wyników po odfiltrowaniu
- Konferencje 3 wyników po odfiltrowaniu
- Osoby 115 wyników po odfiltrowaniu
- Wynalazki 14 wyników po odfiltrowaniu
- Projekty 19 wyników po odfiltrowaniu
- Laboratoria 3 wyników po odfiltrowaniu
- Zespoły Badawcze 1 wyników po odfiltrowaniu
- Aparatura Badawcza 1 wyników po odfiltrowaniu
- Kursy Online 456 wyników po odfiltrowaniu
- Wydarzenia 15 wyników po odfiltrowaniu
- Dane Badawcze 1392 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: D.C. conductivity
-
Low temperature electrical conductivity of the SrFeO3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrFeO3-d (SFO) pellet. DC electrical conductivity measurements of SFO were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas flow rate of 40...
-
Low temperature electrical conductivity of the SrTi0.65Fe0.35O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.30Fe0.70O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.30Fe0.70O3-d (STF70) pellet. DC electrical conductivity measurements of STF70 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.50Fe0.50O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.50Fe0.50O3-d (STF50) pellet. DC electrical conductivity measurements of STF50 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.10Fe0.90O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.10Fe0.90O3-d (STF90) pellet. DC electrical conductivity measurements of STF90 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Electrical conductivity of the SrTi1-xFexO3-d pellets at 20% pO2
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense SrTi1-xFexO3-d (x=0.35, 0.50, 0.70) pellets. DC electrical conductivity measurements were performed by the Van der Pauw method between 900 °C and 200 °C. Studies were performed at 20% of oxygen partial pressure under humidified (~4 vol%) gas flow rate of 50 ml min -1.
-
Investigation of the thermal conductivity of λ gypsum using the hot wire method
Dane BadawczeAn experimental study was conducted to determine the thermal conductivity coefficient λ using the ‘hot wire’ method for a building material. Gypsum specimens measuring 400 x 60 x 50 mm were made for the experiment. Along the long axis of the model, an insulated resistance wire with a diameter of 0.2 mm was poured into the gypsum slurry in the centre...
-
Electrical conductivity of the Sr0.86Ti0.65Fe0.35O3-d pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense Sr0.86Ti0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method. Studies were performed at different oxygen partial pressures (20%, 1% and 0.1%) under humidified (~4 vol%) gas flow rate of 50 ml min -1.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Changes on the Surface of the SiO2/C Composite, Leading to the Formation of Conductive Carbon Structures with Complex Nature of DC Conductivity
Dane BadawczeChanges on the Surface of the SiO2/C Composite, Leading to the Formation of Conductive Carbon Structures with Complex Nature of DC Conductivity
-
SEM images of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
Electrical conductivity of the (Ce0.80Gd0.20)O1.90 pellet at different oxygen partial pressures
Dane BadawczeThis dataset contains results electrical conductivity measurements of dense (Ce0.80Gd0.20)O1.90 (CGO-20) pellet. DC electrical conductivity measurements of CGO-20 were performed by the Van der Pauw method between 900 °C and 450 °C with 50 °C step. Studies were performed at different oxygen partial pressures (100%, 20% and 1%) under humidified (~4...
-
Influence of sintering temperature of porous SrTi0.30Fe0.70O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.50Fe0.50O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
SEM image and line EDS of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with line EDS analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 20 kV in a high vacuum mode. The chemical compositions of the investigated powder...
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
A synthetic result of the development of personnel risk factors in the A, B, C, D enterprise
Dane BadawczeThe data below presents the shape of all the researched personnel risk factors in the A, B, C, D enterprise (which were tested by the author). Further considerations should be started with the presentation of the synthesis of the obtained results, which is presented in this research data.
-
SEM image and EDS map of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with EDS map analysis results. This study were performed for better understanding the chemical composition of flat like structures that occurs in electrode. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
SEM images of symmetrical cell interface with SrTi1-xFexO3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi1-xFexO3-d (x=0.35; 0.50; 0..70) electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum...
-
Selection of the lambda parameter for DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure
Dane BadawczeThis dataset contains results of selection of the lambda parameter for Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. Used lambdas: 5 x 10^(-3), 1 x 10^(-3), 5 x 10^(-4) and 1 x 10^(-4)....
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
Thermal conductivity of M0-M100 specimens
Dane BadawczeThermal conductivity and volumetric heat capacity values of M0, M20, M40, M60, M80, M100 samples
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Dane BadawczeThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 600 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 600 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results converted...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using three R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated three R-CPE elements from equivalent circuit,...
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using two R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated two R-CPE elements from equivalent circuit,...
-
Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis dataset includes electrical conductivity measurements results measured by van der pauw technique up to 900oC.