Microstructure and electrical properties of manganese borosilicate glasses
The structure, optical and electrical properties of manganese borosilicate glasses of the composition xMnO–(80 − x)SiO 2 –20B 2 O 3 (x = 40, 50, and 60 mol%) were investigated. The dependence of the glass structure on its composition was discussed and related to electrical properties. A separation of two amorphous phases was observed. It was suggested that one phase is MnO-rich and the other is SiO 2 -rich. It was found that...
-
Electronic and ionic relaxations in strontium-borate glass and glass-ceramics containing bismuth and vanadium oxides
The topography, microstructure and electrical properties of strontium-borate glass and SBO glass containing bismuth and vanadium oxides, were studied. The structure was measured using X-ray diffraction (XRD), Energy Dispersive X-ray Spectrometer (EDS) and Scanning electron microscope (SEM) methods. The A.C. complex conductivity was investigated as a function of temperature and frequency. The influence of the quantity of bismuth...
-
Electrical properties of Na2O-CaO-P2O5 glasses doped with SiO2 and Si3N4
Sodium-calcium-phosphate glasses doped with SiO2 or Si3N4 having similar sodium ion concentrations were prepared by melt quenching. The conductivity was measured by impedance spectroscopy under nitrogen atmosphere in a wide frequency range (10 mHz–1 MHz) and wide temperature range (153–473 K). At 36.6 °C, DC conductivities of all glasses vary between 1.1 ∗ 10−12 and 8.9 ∗ 10−12 S cm−1 and have similar activation energies (between...