Wyniki wyszukiwania dla: METALLIC NANOSTRUCTURES
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
TEM imaging of metal nanoparticle cross section
Dane BadawczeTEM microscope was used for a imaging of metallic nanostructures. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Interface diffusion between metallic nanoparticles and silicon substrate
Dane BadawczeInterface diffusion between metallic nanoparticles and silicon substrate was detected by EDX method. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Formation of gold nanostructures detected by XPS method
Dane BadawczeGold nanostructers were manufactured by thermal dewetting of thin film. Film with thickness of 2.8 nm was deposited by magnetron sputtering method. As a result of annealing at 550 deg, nanostructures appear. Bulk gold, as-deposited gold film and metallic nanostructures were measured by XPS method.
-
Dewetting of silver films detected by XPS method
Dane BadawczeDewetting of silver thin films was detected by XPS method. Thin metallic films were deposited by magnetron sputtering method. Formation of nanostructures , as a result of thermal annealing, was confirmed by SEM microscope. For comparision three samples were measured. Bulg gold, as-deposited silver film with thickness of 3 nm and nanostructures.
-
Morphology of the gold nanoislands
Dane BadawczeDewetting of the thin metallic films leads to formation of an isolated islands. morphology of nanostructures was measured by SEM microscope. Thin gold films with a thickness of 1.2 nm, 1.5 nm and 3.4 nm were anealed at 550, 600 and 650 Celcius degress.