DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Maximum forces in tendon connections for an anchor with a pin in the full sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element with a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were subjected...
-
Maximum forces in tendon connections for an anchor without pin in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element without a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were...
-
Maximum forces in tendon connections for an anchor with pin in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element with a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were subjected...
-
Maximum forces in tendon connections for the Kessler suture in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the traditional two-strand Kessler sutures (3-0 sutures) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples...
-
Thermogravimetric analysis data of hydration in air and nitrogen for BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were conducted on Netzsch STA 449.
-
Forming of the gap in tendon sutures with the Kessler suture
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the gap formation process between the fronts of the connected tendons was observed. Tendons from fresh swine legs (commercially available) served as the biological material. The tendon juncture...
-
Forming of the gap in tendon sutures with an anchor without a pin
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the gap formation process between the fronts of the connected tendons was observed. Tendons from fresh swine legs (commercially available) served as the biological material. The tendon juncture...
-
Forming of the gap in tendon sutures with an anchor with a pin
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the gap formation process between the fronts of the connected tendons was observed. Tendons from fresh swine legs (commercially available) served as the biological material. The tendon juncture...
-
Sliding friction of alumina (Al2O3) with friction induced vibrations
Dane BadawczeTest files containing data on experiments in self mated sliding contact of alumina Al2O3 lubricated with either water or paraffin oil. Tests run in variable load/velocity conditions and with different dynamic settings of the test rig (PT-3 tribometer). The aim of the research was to attempt in finding correlations between the dynamic characteristics...
-
Permanent traffic counting stations - Expressway S6 in Gdansk (dataset containing 5-min aggregated traffic data and weather information)
Dane BadawczeThe data includes traffic data from permanent traffic count station located on the expressway S6 in the Tri-City Agglomeration area in Poland. The data covers the three year period between 2014 and 2017 and one direction of traffic (southbound).