Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel
PublikacjaFatigue behaviour of SLM 18Ni300 steel under proportional bending-torsion loading is studied. The fatigue tests are conducted under pulsating loading conditions using tubular specimens with a transversal circular hole. Three ratios of the normal stress to shear stress are considered, namely σ/τ=4,σ/τ=2 and σ/τ = 4/3. Crack initiation sites were found for two diametrically opposite points around the hole, whose locations are governed...
-
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
PublikacjaIn this study, different fracture surfaces caused by fatigue failure were generated from 18Ni300 steel produced by selective laser melting (SLM). Hollow round bars with a transverse hole were tested under bending-torsion to investigate the crack initiation mechanisms and fatigue life. Next, the post-failure fracture surfaces were examined by optical profilometer and scanning electron microscope. The focus is placed on the relationship...
-
Strain energy density and entire fracture surface parameters relationship for LCF life prediction of additively manufactured 18Ni300 steel
PublikacjaIn this study, the connection between total strain energy density and fracture surface topography is investigated in additively manufactured maraging steel exposed to low-cycle fatigue loading. The specimens were fabricated using laser beam powder bed fusion (LB-PBF) and examined under fully-reversed strain-controlled setup at strain amplitudes scale from 0.3% to 1.0%. The post-mortem fracture surfaces were explored using a non-contact...
-
The Smith-Watson-Topper parameter and fracture surface topography relationship for additively manufactured 18Ni300 steel subjected to uniaxial variable-amplitude loading
PublikacjaIn this paper, the association between Smith-Watson-Topper (SWT) parameter and fracture surface topography is studied in additively manufactured maraging steel exposed to variable-amplitude fatigue loading. The post-failure fracture surfaces were examined using a non-contact 3D surface topography measuring system and the entire fracture surface method. The focal point is on the correspondence between fatigue characteristics, articulate...
-
A brief note on entire fracture surface topography parameters for 18Ni300 maraging steel produced by LB-PBF after LCF
PublikacjaThe concept of entire fracture surface investigation is helpful in explaining fatigue phenomena. In this paper, this method has been applied for 18Ni300 maraging steel using a 3D measurement system. Before post-mortem analysis, the specimens produced by laser beam powder bed fusion (LB-PBF) were tested under low-cycle fatigue (LCF) for eight strain amplitudes in the interval 0.3% to 1.0%. The attention was placed on the relationship...
-
Fatigue behaviour of SLM maraging steel under variable-amplitude loading
PublikacjaOne of the most challenging issues for additive manufactured materials is fatigue endurance. Engineering components often operate under complex, variable amplitude loadings, in which existing technological imperfections promote fatigue cracks growth and damage of elements eventually. In this study the effects of different variable-amplitude strain levels on fatigue life, 18Ni300 steel was tested. The work presents various behaviours...
-
Cyclic deformation and fracture behaviour of additive manufactured maraging steel under variable-amplitude loading
PublikacjaThe cyclic deformation and fracture behaviour of 18Ni300 maraging steel produced by laser beam powder bed fusion is studied under variable-amplitude loading. The tests were conducted under fully-reversed strain-controlled conditions with a loading sequence comprising three ascending cycles and three descending cycles repeated sequentially until failure. After the tests, fracture surfaces were examined using height and volume surface...
-
The correlation of fractal dimension to fracture surface slope for fatigue crack initiation analysis under bending-torsion loading in high-strength steels
PublikacjaIn this study, the fractal dimension of fatigue fracture surfaces is investigated in order to find an alternative failure loading indicator. Some of many metrological factors are generalized by reducing the fracture surface structure to one factor and develop an entire fracture surface procedure by analyzing the impact of surface slope and calculation resolution. Three notched geometries are studied under cyclic bending-torsion:...