Wyniki wyszukiwania dla: NDFEB ALLOY

• JOURNAL OF ALLOYS AND COMPOUNDS

  Czasopisma

  ISSN: 0925-8388 , eISSN: 1873-4669

• One-step recovery of REE oxalates in electro-leaching of spent NdFeB magnets

  Publikacja

  • I. Makarova
  • J. Ryl
  • Z. Sun
  • I. Kurilo
  • K. Górnicka
  • M. Laatikainen
  • E. Repo

  - SEPARATION AND PURIFICATION TECHNOLOGY - Rok 2020

  Recovery of rare-earth elements (REEs) from spent NdFeB magnets is receiving great attention because of high amount of neodymium and potential risk of environmental pollution. In this study, a novel environment-friendly hydrometallurgical route is proposed for efficient recovery of REEs during electrochemical leaching with sulfuric and oxalic acids. With proper adjustment of the electrolyte composition and operating conditions,...

  Pełny tekst do pobrania w portalu

• Tracking of the Multimodal Ordering Process in FePd Alloy

  Publikacja

  • M. Perzanowski
  • A. Zarzycki
  • M. Krupinski
  • M. Wolny-Marszalek

  - Journal of Physical Chemistry C - Rok 2024

  Pełny tekst do pobrania w portalu

• Internal friction in FePd alloy during ordering

  Publikacja

  • E. Klugmann
  • M. Polowczyk

  - TRIBOLOGIA - Rok 2002

  Stwierdzono występowanie wysokiego poziomu tarcia wewnętrznego w zahartowanym stopie FePd (50% at. Pd). Zbadano proces uporządkowania atomowego w korelacji ze zmianami tarcia wewnętrznego defektu modułu i relaksacji magnetycznej stopu porządkującego się podczas nagrzewania do 900 K. Zaobserwowano efekt prędkości nagrzewania na punkt Curie.

• Phase investigations of copper based CuZn38Al2MnFe alloy

  Publikacja

  • M. Szkodo
  • M. Głowacka
  • M. Smajdor
  • H. Bugłacki

  - Solid State Phenomena - Rok 2006

  W pracy przedstawiono analizę fazową mosiądzu CuZn38Al2MnFe. Wykazano, że obecność fazy Fe4Mn77Si19 powoduje kruchość stopu w teście zginania próbek.

  Pełny tekst do pobrania w serwisie zewnętrznym

• Environmental degradation of titanium alloy in artificial saliva

  Publikacja

  • A. Zieliński
  • Ł. Zborowski - Weychman

  - Advances in Materials Science - Rok 2012

  The titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization...

  Pełny tekst do pobrania w portalu

• Elctrochemical oxidation and corrosion resistance of the Ti13Nb13Zr alloy

  Publikacja

  • A. Ossowska
  • A. Zieliński
  • M. Supernak

  - Engineering of Biomaterials / Inżynieria Biomateriałów - Rok 2013

  This paper presents the results of oxidation and corrosion tests carried out on titanium alloy Ti13Nb13Zr. The oxide film was prepared by electrochemical environment 2M H3PO4 for 30 min and 1 h, at a constant voltage 40V. The tests of corrosion resistance were performed by potentiostatic method in Ringer's solution at different pH values: 7, 5 and 3. The change in an appearance of surface and the increase in corrosion resistance...

  Pełny tekst do pobrania w serwisie zewnętrznym

• Oxidation and hydrogen behavior in Zr-2Mn alloy

  Publikacja

  • N. Zienkiewicz
  • J. Paradowska
  • W. Serbiński
  • G. Gajowiec
  • A. Hernik
  • A. Zieliński

  - Advances in Materials Science - Rok 2018

  The purpose of the present research was to determine the oxidation and hydrogenation behavior in the new Zr-2Mn alloy. The oxidation of alloy was performed at temperatures between 350°C and 900°C for 30 minutes. The hydrogen charging was made for 72 h at a current density 80 mA/cm2. The charged samples were heat treated at 400°C for 4 h to obtain a uniform hydrogen profile content across the sample. The oxidation resulted in an...

  Pełny tekst do pobrania w portalu

• Elasto-viscoplastic properties of AA2017 aluminium alloy

  Publikacja

  • A. Ambroziak
  • P. Kłosowski
  • Ł. Pyrzowski

  - TASK Quarterly - Rok 2011

  Artykuł opisuje procedurę identyfikacji parmetrów materiałowych dla sprężysto-lepkoplastycznego modelu Bodnera-Partoma. Prezentowane są symulacje numeryczne testów jednoosiowego rozciągania z różnymi prędkościmi odkształcenia, które porównane są z wynikami eksperymantalnymi.

  Pełny tekst do pobrania w portalu

• Properties of Composite Oxide Layers on The Ti13Nb13Zr Alloy

  Publikacja

  • A. Ossowska
  • R. Beutner
  • D. Scharnweber
  • A. Zieliński

  - SURFACE ENGINEERING - Rok 2017

  The development of composite oxide layers on the Ti13Nb13Zr alloy, their structure and properties have been demonstrated. Two subsequent methods were applied to prepare the composite layers. During the first stage gas oxidation produced a solid oxide layer, and subsequently oxide nanotubes were produced by using an electrochemical method. Scanning electron microscopy (SEM), chemical analysis, energy dispersive X-ray spectroscopy...

  Pełny tekst do pobrania w serwisie zewnętrznym