Filtry
wszystkich: 3789
wybranych: 175
-
Katalog
- Publikacje 2528 wyników po odfiltrowaniu
- Wydawnictwa 4 wyników po odfiltrowaniu
- Osoby 276 wyników po odfiltrowaniu
- Wynalazki 14 wyników po odfiltrowaniu
- Projekty 150 wyników po odfiltrowaniu
- Zespoły Badawcze 21 wyników po odfiltrowaniu
- Aparatura Badawcza 1 wyników po odfiltrowaniu
- Kursy Online 610 wyników po odfiltrowaniu
- Wydarzenia 10 wyników po odfiltrowaniu
- Dane Badawcze 175 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: Aleksandr Sołżenicyn
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
SEM image and line EDS of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with line EDS analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 20 kV in a high vacuum mode. The chemical compositions of the investigated powder...
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Selection of the lambda parameter for DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure
Dane BadawczeThis dataset contains results of selection of the lambda parameter for Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. Used lambdas: 5 x 10^(-3), 1 x 10^(-3), 5 x 10^(-4) and 1 x 10^(-4)....
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 600 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 600 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results converted...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 15% oxygen partial pressure
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using three R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated three R-CPE elements from equivalent circuit,...
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using two R-CPE fiting elements
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated two R-CPE elements from equivalent circuit,...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element series resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes at different oxygen partial pressures
Dane BadawczeIn this dataset are presented results of the polarization resistance of SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at 800 °C. The measurement temperature range was between 800 °C and 500 °C. Applied different oxygen partial pressure flow was: 1%, 20% and 100% pO2. Results converted to electrode surfaces area and dived by two electrodes. All...
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
Simulations of flows in the coastal zone of the Baltic Sea
Dane BadawczeThe study area is located in the Southern Baltic, within Polish Marine Areas, adjacent to the coastline in the vicinity of Lubiatowo village, where The Coastal Research Station (CRS) – a field laboratory of the Institute of Hydro-Engineering of the Polish Academy of Sciences (IBW PAN) –is situated. The numerical reconstruction of the coastal flow was...
-
Replication package accompanying the paper: Parteka A., Zarach, Z.H., Kordalska A. (2024). Technological content of export diversification.
Dane BadawczeThis replication package contains data and codes allowing to replicate the analysis described in the paper: Parteka A., Zarach, Z.H., Kordalska A. (2024). Technological content of export diversification.
-
Concrete temperature measurements of cubic specimens cured under isothermal and semi-adiabatic conditions
Dane BadawczeThe DataSet contains temperature measurements of concrete cubes (150 x 150 x 150 mm) cured under isothermal and semi-adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...
-
Measurements of the heat of hydration released by concrete specimens cured under adiabatic conditions
Dane BadawczeThe DataSet contains measurements of heat of hydartion of concrete cubes (150 x 150 x 150 mm) cured under adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...
-
Permanent traffic count stations - expressway S6 Poland 2016
Dane BadawczeThe data includes traffic data from permanent traffic count stations located on the expressway S6 in the Tri-City Agglomeration area in Poland. The data covers the 12 months of 2016.
-
X-ray diffractometry results of the Sr0.86Ti0.65Fe0.35O3 powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.86Ti0.65Fe0.35O3-d (STF35) powder. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. It confirms the formation of the cubic perovskite oxide phase. Calculated average lattice constant is a 3.90882(1) Å, with Goodness of Fit...
-
SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrodes sintered at 1050 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrode sintered at 1050 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using...
-
SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
Functional specialisation and economic upgrading in GVCs
Dane BadawczeThe dataset collected for selected Central Eastern European (CEE) countries (CZE, EST, HUN, LVA, LTU, POL, SVK, SVN) contains country-level and sector-level observations for the project implementation linked to the concept of functional specialization of economies. The aim of the project is to identify patterns of functional specialisation in global...
-
SEM images of cross sections of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains cross sectional images of the porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes symmetric cells samples interface. Here are presented images of electrodes sintered at 950 °C, 1000 °C and 1050 °C. Images were obtained using a FEI Quanta FEG 250 Scanning Electron Microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum...
-
Data on bicycle traffic in Lodz (Poland) paired with weather and air quality data
Dane BadawczeThe file contains data on bicycle traffic registered by counting stations loacted in Lodz in the years 2016-2019. The data are paired with weather and air quality data from Lodz collected for the same period. The data is described below:
-
Low temperature electrical conductivity of the SrFeO3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrFeO3-d (SFO) pellet. DC electrical conductivity measurements of SFO were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas flow rate of 40...
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Data on bicycle traffic in Gdansk paired with weather and air quality data
Dane BadawczeThe file contains data on bicycle traffic registered by counting stations loacted in Gdańsk in the years 2013-2020. The data are paired with weather and air quality data from Gdansk collected for the same period. The data is described below:
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Low temperature electrical conductivity of the SrTi0.65Fe0.35O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.30Fe0.70O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.30Fe0.70O3-d (STF70) pellet. DC electrical conductivity measurements of STF70 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.50Fe0.50O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.50Fe0.50O3-d (STF50) pellet. DC electrical conductivity measurements of STF50 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Dane BadawczeThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Permanent traffic counting stations - Expressway S7 in Gdansk, Poland
Dane BadawczeThe data includes traffic data from permanent traffic count station located on the expressway S7 in the Tri-City Agglomeration area in Poland. The data covers the 2 months of 2015 (May, October) and one direction of traffic (eastbound).
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Low temperature electrical conductivity of the SrTi0.10Fe0.90O3-d pellet
Dane BadawczeThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.10Fe0.90O3-d (STF90) pellet. DC electrical conductivity measurements of STF90 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Magnetic field maps of an astable multivibrator in frequency range from 30 MHz to 3 GHz – selective detection
Dane BadawczeThe data presents a result of near field measurements of electromagnetic emissions radiated from the PCB of a small electronic device. An efficient method of modelling the magnetic and electric field emissions is the measurements in the near field using electric and magnetic probes. The attached files contain magnetic field maps created on based measurements...
-
Permanent traffic counting stations - Expressway S6 in Gdansk (dataset containing 5-min aggregated traffic data and weather information)
Dane BadawczeThe data includes traffic data from permanent traffic count station located on the expressway S6 in the Tri-City Agglomeration area in Poland. The data covers the three year period between 2014 and 2017 and one direction of traffic (southbound).
-
Laser microscope profilometry of (Ce0.80Gd0.20)O1.90 surface before polishing
Dane BadawczeThe dataset consists of a surface image and topography obtained using a Keyence VK-X1000 confocal laser microscope for (Ce0.80Gd0.20)O1.90 substrate (CGO-20). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable focus. The...