Chemical composition analysis of the LSNO ceramics
Dane BadawczeThe chemical composition of a series of La-Sb-Nb-O ceramics manufactured by the solid-phase reaction method was analyzed. The samples with a various antimony content were measured by XPS method (OmicronNanotechnology UHV system). Analysis confirmed presence of elements: La, Sb, Nb.
-
Comparisson of area specific resistance of the SrTi1-xFexO3-d porous oxygen electrodes and state-of-the-art LSCF sintered at optimal conditions
Dane BadawczeIn this dataset are presented results of the polarization resistance of optimaly sintered SrTi1-xFexO3-d porous oxygen electrodes in symetrical cell (1000 °C; 800 °C and 800°C respectively x = 0.35; 0.50 and 0.70). For commparison were selected commercially avilable state-of-the-art LSCF (Europa) sintered at 1050 °C. The measurement temperature range...
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Dane BadawczeThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...