Wyniki wyszukiwania dla: nanopowder
-
The SEM images of Ce0.8La0.2O2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed...
-
The SEM images of CeO2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of CeO2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed several...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The TPR reduction profile of Ce0.9M0.1O2
Dane BadawczeThe dataset includes the TPR reduction profiles of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared by the reverse microemulsion method. After the synthesis powders were dried, then calcined at 500 degrees for 2 h. The measurements were carried out in H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min.
-
The XRD diffraction patterns of Ce0.9M0.1O2 prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution using tetramethylammonium hydroxide (TMAOH). After the precipitation, the sediment was centrifuged and rinsed with alcohol several times. Precursors powder...
-
The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.