Search results for: NANOTUBULAR TITANIUM OXIDE
-
Nanotubular oxide layer formed on helix surfaces of dental screw implants - SEM examination
Open Research DataThe samples used for the research had the shape of a helix with a metric thread, with their geometry imitating a dental implant. The oxide layer was produced by a standard electrochemical method in an environment of 1M H3PO4 + 0.3 % HF for 20 min, at a constant voltage of 30 V. The oxidized samples were analyzed with a scanning electron microscope.
-
XPS study of the TiO2-WO2 composites
Open Research DataValence state of W and Ti was measured in a TiO2-WO3 composites with a various composition.Powder samples of pure titanium dioxide, tungsten oxide and mix of 50% titanium oxide and 50% od tungsten oxide were measured. Oxides were annealed at the temperature in the range of 300 Celsius degree up to 900 deg. Measurements were performed by XPS UHV Omicron...
-
XPS measurement of the Fe-Ti based materials
Open Research DataThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
Structural investigations of the LTO:Cu thin films
Open Research DataLithium titanate (Li1+xTi2-xO4) doped with Cu2+ ions was synthesized by sol-gel processing method. The structure was characterized by X-ray Diffraction (XRD). All samples revealed presence of LTO spinel phase. X-ray pattern of undoped LTO was free of any impurities and other crystal phases. Similarly, samples with low amount of copper dopant (x = 0.05...
-
UV/VIS Spectroscopy of titanium dioxide coated nickel foams
Open Research DataThe data includes UV-Vis spectra of titanium dioxide coated nickel foams heated at 400, 500 and 600 C in Ar. Jasco V-650 Spectrophotometer was used and Spectra Measurement software.
-
Depth XPS profile of Fe-S layers on a titanium substrate
Open Research DataDepth XPS profile of Fe-S layers on a titanium substrate was measured. Material was etched by Argon ion gun and measured by XPS method. For each sample, three times per 10 minutes each was sputtered.
-
XRD (X-ray Diffraction) of titanium dioxide coated nickel foams
Open Research DataThese data include XRD patterns of titanium dioxide coated nickel foams heated at 400, 500 and 600C in argon atmosphere.
-
BET specific surface area measurements of bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Open Research DataThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
FTIR (Fourier-transform infrared spectroscopy) spectra of titanium dioxide coated nickel foams.
Open Research DataThis dataset contains FTIR spectra recorded on a JASCO 4200 spectrometer of nickel foams coated with titanium dioxide after heating at 400, 500 and 600 C and after photocatalytic process with NOx.
-
BET specific surface area measurements of silica-coated bismuth oxide(Bi2O3) and gadolinium oxide (Gd2O3) structures
Open Research DataThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
XPS (X-ray photoelectron spectroscopy) of titanium dioxide coated nickel foams and heated 400,500, 600C
Open Research DataThis data set contains XPS spectra recorded for nickel foams coated with titanium dioxide and heated at 400, 500 and 600 degrees celcius.
-
BET (Brunauer-Emmett-Teller) surface area analysis of titanium dioxide coated nickel foams
Open Research DataThe data are presented for the BET surface results of nickel foams coated with titanium dioxide and heated 400, 500 and 600 degrees Celsius in an argon atmosphere. N2 sorption was performed at 77 K pore size distribution was determined by BJH and DFT methods.
-
SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2)
Open Research DataData contain SEM and SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2). The detailed equipment and measurement data was described in measurement info.txt file.
-
BET specific surface area measurements of silica-coated bismuth oxide (Bi2O3)/gadolinium oxide (Gd2O3) core-shell structures
Open Research DataThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
Electrochemical measurements of borophene functionalized with nickel(II) oxide (NiO)
Open Research DataThis dataset contains linear sweep voltammetry (LSV) and chronopotentiometry (CP) technique results for borophene functionalized with nickel(II) oxide (NiO) and reference samples: ruthenium(IV) oxide (RuO2), nickel(II) oxide (NiO) and pristine borophene. Linear sweep voltammetry (LSV) results show the oxygen evolution reaction permormance of the obtained...
-
Graphene oxide thin films deposited on a PCB board - chemical analysis
Open Research DataGraphene oxides based films were measured by X-ray photoemission spectroscopy (XPS) method. TheXPS measurements were carried out with the Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The...
-
The effect of zinc oxide concentration on dry matter content of chitosan gels in carbonic acid.
Open Research DataThe dataset contains results determining the effect of zinc oxide addition at different concentrations on the dry matter content of chitosan gels in carbonic acid after a specified time. Zinc oxide at concentrations of 0.5 and 1% was added as a powder to a 1% solution of chitosan in carbonic acid and then homogenized. Differences were observed in the...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Open Research DataData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
Nanoindentation tests of the hydroxyapatite composite coatings applicated on titanium alloys by the electrophoretic method
Open Research DataCurrently, there are no metal materials that meet all biomechanical and biochemical requirements needed for long life implantable biomaterials. The main purpose of the study was to functionalize the surface of the titanium alloys used in biomaterial implants.
-
Topography and microstructure of phosphate-iron glasses containing niobium and titanium
Open Research DataThe topography and microstructure of phosphate-iron glasses containing niobium and titanium were investigated by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM). Glass samples of the composition of 35P2O5-30Fe2O3-(35-x)Nb2O5-xTiO2 where x= 0; 7.5 and 15 (in %mol) were prepared by the conventional melt quenching technique. Appropriate...