AFM images of the platinum (111) single crystal surface as delivered, without the polishing treatment
Open Research DataPlatinum (111) single crystal surface images as delivered, without polishing treatment. Topographic measurements in contact mode. NTEGRA Prima (NT-MDT) device. CSG probe 10.
-
The AFM micrographs of V2O5 single crystals
Open Research DataThe DataSet contains the atomic force microscope images of the surface of V2O5 single crystals. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The As-prepared films were deposited on a quartz glass substrate and were annealing at 600°C under synthetic air.
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Open Research DataThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...
-
X-ray diffraction (XRD) of bulk boron and borophene flakes after the ball-milling process at different operating parameters
Open Research DataThese data include X-ray diffraction patterns of bulk boron and borophene obtained during ball milling at different rotation speeds, time and mass loadings. The data were collected to investigate the crystal structure of the studied materials.
-
The luminescence study of Ga2–x(Al0.68In0.32)xO3:Cr3+ coumpounds.
Open Research DataNear-infrared (NIR) phosphor-converted light-emitting diodes (pc-LEDs) are a highly efficient perspective NIR light source, with application hindered by a narrow emission band. In this work, we broaden the emission of a new series of NIR phosphors by controlling crystal structure disorder through cation cosubstitution. By substituting Ga3+ with (Al0.68In0.32)3+,...
-
SEM micrographs of NH4VO3 crystals
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the type of ammonium salt and the solvent. It can be concluded that the used solvent affected crystal shapes and their size was...
-
SEM images of dewetted gold films
Open Research DataGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Oxidation of silver nanostructures
Open Research DataSilver nanostructures were prepared on Si substrate. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma. The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1 , and the incident power was in the range of 30–40 W. The layer thickness...
-
Structural investigations of the LTO:Cu thin films
Open Research DataLithium titanate (Li1+xTi2-xO4) doped with Cu2+ ions was synthesized by sol-gel processing method. The structure was characterized by X-ray Diffraction (XRD). All samples revealed presence of LTO spinel phase. X-ray pattern of undoped LTO was free of any impurities and other crystal phases. Similarly, samples with low amount of copper dopant (x = 0.05...
-
The scanning tunnelling micrographs of highly oriented pyrolytic graphite
Open Research DataThe dataset contains the results imaging of a sample of highly oriented pyrolytic graphite obtained using scanning tunneling microscopy. The above variant of scanning probe microscopy is one of the most convenient research techniques at atomic scales. The file contains images corresponding to increasing magnifications from the 1 um scale to a few nanometers....
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Open Research DataAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Investigation of plasmon resonance in a silver nanoparticles
Open Research DataSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
SEM images of tge gold nanostructures on silicon
Open Research DataAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
Formation of gold anostructures detected by SEM microscope
Open Research DataGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
Opposite pressure impact on electron-phonon coupling in Eu2+ and Ce3+ doped AlN
Open Research DataThis data analyzes the influence of pressure on electron–lattice interactions in the 5d excited states of Ce3+ and Eu2+ in the AlN host based on pressure-dependent photoluminescence and photoluminescence excitation spectra. High-pressure measurements on AlN samples doped with Eu2+ and Ce3+ ions reveal that the Stokes shift increases with pressure for...
-
The luminescence study of Ga1.98–xAlxO3:0.02Cr3+ coumpounds.
Open Research DataA chemical and mechanical pressure-induced photoluminescence tuning method was developed through structural evolution and hydrostatic pressure involving phase transition. A series of Ga1.98−xAlxO3:0.02Cr3+ phosphors were synthesized by collaborators from National Taiwan University. Structural evolution reveals a crystal phase change with the incorporation...
-
X-ray diffraction patterns of BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Open Research DataThe dataset consists of three raw X-ray diffraction (XRD) files collected using a Phillips X’Pert Pro diffractometer (CuKα radiation (𝜆 = 1.541 Å), under 40 kV and 30 mA). The diffraction patterns of BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were collected at room temperature. Collected...
-
The chemical and mechanical pressure influence on chromium luminescence
Open Research DataIn this study, we aim to compare the changes in the luminescence properties of Ga2O3:Cr3+ modified by Al or Sc ion substitution (chemical pressure) and hydrostatic pressure. We find the same behavior for Ga2–xAlxO3:Cr3+ and different behavior for Ga2–xScxO3:Cr3+ in terms of the optical properties under chemical and mechanical pressure. We consider Al...
-
Mechanical properties of single V2O5 nanocrystal - nanoindentation measurement in control of the max-load
Open Research DataThe DataSet contains the nanoindentation curves (indentation force Fn vs penetrationPd) for a single V2O5 nanocrystal supported on a substrate. The measurements were performed in control of the maximum load of Berkovich indenter force from 2 to 50 mN.
-
Mechanical properties of single V2O5 nanocrystal - nanoindentation measurement in control of the max-depth
Open Research DataThe DataSet contains the nanoindentation curves (indentation force Fn vs penetrationPd) for a single V2O5 nanocrystal supported on a substrate. The measurements were performed in control of the maximum depth of Berkovich indenter penetration: 60, 70, and 100 nm.