D.C. electrical measurements of Bi2VO5.5 ceramic measured at high temperature region

Opis

D.C. electrical properties of Bi2VO5.5 ceramic was measured. 

The polycrystalline Bi2VO5.5 ceramic was synthesised via a conventional solid state reaction route. The stoichiometric mixture of initial powders of Bi2O3 and V2O5 were ball-milled in pure acetone for 6 h. The milling was performed in steps of 1 h with rest intervals of 10 min. The mixture was initially heated up to 770 K and then to 1020 K in air. It was kept at this temperature for 24 h and grinded next. The calcined powder was mixed with a small amount of ethyl alcohol binder and cold-pressed into pellets (12 mm in diameter and 2–3 mmin thickness) under a compacting pressure of 26 kNcm−2. The obtained pellets were sintered at 1070 K for 24 h with heating and cooling rates of 50 Kh−1.

For the electrical measurements gold electrodes were evaporated at the preheated samples. D.C. measurements were carried out with the use of Hioki 3522–50 LCR HiTester. Measurements were done in temperature range from 370 K to 920 K in air atmosphere. The temperature was controlled with the use of high temperature Novotherm HT 1600.

Plik z danymi badawczymi

112.zip
117.3 kB, S3 ETag 0876323864437e68549956cfd538b605-1, pobrań: 6
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik 112.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2015
Data zatwierdzenia:
2021-07-14
Język danych badawczych:
angielski
Dyscypliny:
  • Inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/94gm-rq84 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

wyświetlono 35 razy