Linear impedance of 40Na2O-20CaO-40P2O5 glass measured with impedance spectroscopy method at low temperature region

Opis

The linear electrical properties of 40Na2O-20CaO-40P2O5 glass was measured by impedance spectroscopy method.

The glass composition of 40Na2O-20CaO-40P2O5 (in mol%) was prepared by the conventional
melt quenching technique. Appropriate amounts of reagents: NaH2PO4 (≥99.5% SIGMA ALDRICH), Na2CO3 (99.9+% ChemPur GmbH) and CaCO3 (99.9+% ChemPur GmbH) were thoroughly mixed. Batches were melted in porcelain crucibles at temperatures of 850–950 degC for 30–60 min, in air atmosphere. Melt was poured on a brass plate. The exact composition of melted samples was tested with the use of SEM-EDS and was found to be Na18.5Ca5P16.8O59.5 (in at%).

For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the temperature range from 213 K to 423 K, in the frequency range from 10mHz to 1 MHz and with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.

Plik z danymi badawczymi

124.zip

173.1 kB, S3 ETag 7c585fae9637b481b2baaa5f57b8035f-1, pobrań: 47

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2018

Data zatwierdzenia:

2021-07-19

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)