The electrochemical studies for chitosan hydrogel membranes on glassy carbon substrates

Opis

This dataset contains various electrochemical studies carried out to investigate the preconcentration of [Fe(CN)6]3- ions by chitosan hydrogel membranes coating the glassy carbon electrodes.

The glassy carbon electrode (GCE, 3.0 mm diameter) was first polished with Al₂O₃ powder (0.3 mm) using a polishing kit from Buehler, rinsed with deionized water from Hydrolab Poland, and then dried under a continuous stream of nitrogen at room temperature. Then 5 μL of chitosan hydrogel was applied to the surface thus prepared using an automatic pipette and dried in a stream of nitrogen at room temperature for 30 min. The measuring system consisted of a self-designed vessel, the GCE and Ag/AgCl electrodes from Mineral, and the Pt wire came from Mennica Polska.

These measurements were taken using a Methron Autolab potentiostat/galvanostat, M204 equipped with FRA32M electrochemical impedance spectroscopy module with operating system Nova 2.15. The electrochemical studies of the prepared electrodes were evaluated in a three-electrode system, with a modified GCE as a working electrode, an Ag/AgCl (0.1 M KCl) reference electrode, and a platinum mesh as a counter electrode. The influence of surface engineering by hydrogel coating on the electrode kinetics was evaluated using cyclic voltammetry (CV), differential pulse voltammetry (DPV), and electrochemical impedance spectroscopy (EIS). Electrochemical studies were carried out with 1 mM K₃[Fe(CN)₆], [K₄Fe(CN)₆], C₁₂H₁₄FeO_2, and [Ru(NH₃)₆]Cl₂ dissolved in 0.1 M KCl or PBS as the primary electrolyte. Cyclic voltammograms were registered with scan rates between 10 and 1000 mV/s, and in the potential range −0.35 V to 0.65 V. DPV experimental conditions were: scan rate 10 mV/s, step potential 0.005 V, modulation amplitude 0.025 V, modulation time 0.05 s and interval time 0.5 s, polarization range from −0.3 V to 0.8 V.

These results are part of the manuscript: https://www.sciencedirect.com/science/article/pii/S156753942400166X

Plik z danymi badawczymi

echem.zip

1.4 MB, S3 ETag a3dc77c39e452040d45280e0fe8477fc-1, pobrań: 2

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2024

Data zatwierdzenia:

2024-12-19

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)

DOI:

10.34808/qd01-qe15

Finansowanie:

Technologia addytywnego wytwarzania elektroaktywnych przestrzennych struktur z kompozytów polilaktydu wzmacnianego diamentem

Seria:

Additive manufacturing technology of electroactive three-dimensional structures from diamond reinforced polylactide composites

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 19 razy

Wyszukiwarka