Characteristics of La0.8Sr0.2Ga0.8Mg0.2O3-delta -supported micro-tubular solid oxide fuel cells with bi-layer and tri-layer electrolytes
Abstrakt
In this study, La0.8Sr0.2Ga0.8Mg0.2O3−δ (LSGM)-supported micro tubular solid oxide fuel cells (T-SOFCs) with two different configurations, one containing an LSGM–Ce0.6La0.4O2−δ (LDC) bi-layer electrolyte (Cell A) and one containing an LDC–LSGM–LDC tri-layer electrolyte (Cell B), were fabricated using extrusion and dip-coating. After optimizing the paste formulation for extrusion, the flexural strength of the dense and uniform LSGM micro-tubes sintered at 1500°C was determined to be approximately 144 MPa. Owing to the insertion of an LDC layer between LSGM electrolyte and La0.6Sr0.4Co0.2Fe0.8O3−δ (LSCF)–LSGM cathode, the ohmic resistances of Cell B were slightly larger than those of Cell A at the operating temperatures investigated, mainly because of interfacial resistance, but Cell B exhibited slightly lower polarization resistance than Cell A. The maximum power densities (MPDs) of Cell A were 0.25, 0.35, 0.43, and 0.47 W cm−2 at 650, 700, 750, and 800°C, respectively, which are slightly larger than those of Cell B, i.e., 0.23, 0.33, 0.42, and 0.41 W cm−2, respectively, owing to the facts that Cell A exhibited a slightly higher open-circuit voltage and a smaller Rt value. Cell A containing the LSGM (288 µm)–LDC (8 µm) bi-layer electrolyte can be operated at approximately 650°C with an MPD value of approximately 0.25 W cm−2; however, a similarly structured single cell containing a Zr0.8Sc0.2O2−δ (ScSZ) (210 µm) electrolyte need to be operated at 900°C, and one containing an Ce0.8Gd0.2O2−δ (GDC; 285 µm)–ScSZ (8 µm) bi-layer electrolyte has to be operated at 700°C. Thus, the advantage of using LSGM as an electrolyte for micro T-SOFC single cells is apparent.
Cytowania
-
8
CrossRef
-
0
Web of Science
-
9
Scopus
Autorzy (4)
-
Yi-Xin Liu
- National Taipei University of Technology Department of Materials and Mineral Resources Engineering
-
Sea-Fue Wang
- National Taipei University of Technology Department of Materials and Mineral Resources Engineering
-
Yung-Fu Hsu
- National Taipei University of Technology Department of Materials and Mineral Resources Engineering
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2109/jcersj2.16244
- Licencja
- Copyright (2017 The Ceramic Society of Japan)
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
nr 125,
wydanie 4,
strony 236 - 241,
ISSN: 1882-0743 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Liu Y., Wang S., Hsu Y., Jasiński P.: Characteristics of La0.8Sr0.2Ga0.8Mg0.2O3-delta -supported micro-tubular solid oxide fuel cells with bi-layer and tri-layer electrolytes// JOURNAL OF THE CERAMIC SOCIETY OF JAPAN. -Vol. 125, iss. 4 (2017), s.236-241
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2109/jcersj2.16244
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 127 razy
Publikacje, które mogą cię zainteresować
Design and characterization of apatite La9.8Si5.7Mg0.3O26±δ-based micro-tubular solid oxide fuel cells
- S. Wang,
- Y. Hsu,
- P. Hsia
- + 2 autorów
High-performance NdSrCo2O5+δ–Ce0.8Gd0.2O2-δ composite cathodes for electrolyte-supported microtubular solid oxide fuel cells
- S. Wang,
- Y. Hsu,
- Y. Liao
- + 2 autorów
Effects of La0.8Sr0.2MnO3 and Ag electrodes on bismuth-oxide-based low-temperature solid electrolyte oxygen generators
- J. Tsai,
- S. Wang,
- Y. Hsu
- + 1 autorów
Characteristics of La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ -supported micro-tubular solid oxide fuel cells with LaCo 0.4 Ni 0.6-x Cu x O 3-δ cathodes
- Y. Liu,
- S. Wang,
- Y. Hsu
- + 1 autorów